Abstract

The main scope of the article is the development of a computer system, which should give advices at problem of cooper alloys manufacturing. This problem relates with choosing of an appropriate type of bronze (e.g. the BA 1044 bronze) with possible modification (e.g. calcium carbide modifications: Ca + C or CaC2) and possible heat treatment operations (quenching, tempering) in order to obtain desired mechanical properties of manufactured material described by tensile strength - Rm, yield strength - Rp0.2 and elongation - A5. By construction of the computer system being the goal of presented here work Case-based Reasoning is proposed to be used. Case-based Reasoning is the methodology within Artificial Intelligence techniques, which enables solving new problems basing on experiences that are solutions obtained in the past. Case-based Reasoning also enables incremental learning, because every new experience is retained each time in order to be available for future processes of problem solving. Proposed by the developed system solution can be used by a technologist as a rough solution for cooper alloys manufacturing problem, which requires further tests in order to confirm it correctness.
Go to article

Abstract

This paper presents the influence of annealing time 30, 60 and 120 min at 1000°C for quenching CuAl7Fe5Ni5W2Si2 bronze in 10% water solution of NaCl, on the microstructure and mechanical properties. The presented results concern the species newly developed aluminum-iron-nickel bronze, with additions W and Si. In order to determine changes in the microstructure of the hardened bronze metallographic studies were performed on cylindrical samples of diameter 10 mm, on the metallographic microscope with digital image analysis, X-ray phase analysis, EDX point with the digital recording on the computer. Specified percentage of the microstructure of martensite and bainite, participation of proeutectoid α phase in the microstructure, grain size of former β phase, the amount of dissolved κ phase. It was found that in the microstructure of bronze in the cast state, there are a number of intermetallic phases of κ type. At interphase boundaries of primary intermetallic faceted precipitates, especially rich in tungsten (IM_W), nucleate and grow dendritic primary intermetallic κI phases, with chemical composition similar to the type of Fe3Si iron silicide. Dissolved, during the heating, in the β phase are all the intermediate phase included in the microstructure, with the exception of primary intermetallic phases of tungsten and κI. Prolongation of the isothermal annealing causes coagulation and coalescence of primary phases. In microstructure of the bronze after quenching obtained the α phase precipitation on the grain boundary of secondary β phase, coarse bainite and martensite, for all annealing times. With the change of annealing time are changed the relative proportions of individual phases or their systems, in the microstructure. In the microstructure of bronze, hold at temperature of 1000°C for 60 min, after quenching martensitic microstructure was obtained with the primary phases, and the least amount of bainite
Go to article

Abstract

A possibility to control the strength, hardness and ductility of the L35HM low-alloy structural cast steel by the applied tempering temperature is discussed in the paper. Tests were carried out on samples taken from the two randomly selected industrial melts. Heat treatment of the cast samples included quenching at 900 °C, cooling in an aqueous solution of polymer, and tempering at 600 and 650 °C. The obtained results showed that the difference in the tempering temperature equal to 50 °C can cause the difference of 121 MPa in the values of UTS and of 153 MPa in the values of 0.2%YS. For both melts tempered at 600 °C, the average values of UTS and 0.2%YS were equal to 995 MPa and 933 MPa, respectively. The values of EL and RA did not show any significant differences. Attention was drawn to large differences in strength and hardness observed between the melts tempered at 600 and 650 °C. Despite differences in the mechanical properties of the examined cast steel, the obtained results were superior to those specified by the standard.
Go to article