In this paper crystallization studies of low-alloyed construction cast steel were presented for different additions of chromium, nickel and molybdenum modified with vanadium and titanium. Studies were conducted using developed TDA stand, which additionally enabled evaluation of cooling rate influence on crystallization process of investigated alloys.
The article shows results of studies of primary crystallization and wear resistance of Cr-Ni-Mo cast steel intended for work in corrosive and abrasive conditions. The studies of primary crystallization were conducted with use of TDA method and modified tester allowing measurement casting cooling time influence on the cooling and crystallization curves of studied alloys. After heat treatment of examined cast steel wear tests of the samples were conducted on pin-on-disc type device.
Paper presents the results of studies on primary crystallization and wear resistance of high chromium cast iron inoculated with ferrotitanium intended for work in abrasive conditions. Primary crystallization was examined with use of TDA method, wear tests of the samples were conducted using the modified pin-on-disk method.
The modification is a widespread method of improving the strength properties of cast iron. The impact in terms of increasing amounts of eutectic grains has been thoroughly studied while the issue of the impact on the mechanical properties of primary austenite grains has not been studied in depth yet. The paper presents the study of both aspects. The methodology was to conduct the melting cast iron with flake graphite, then modifying the alloy by two sets of modifiers: the commercial modifier, and a mixture of iron powder with a commercial inoculant. The DAAS test was carried out to identify the primary austenite grains. The degree of supercooling was determined and the UTS test was performed as well. Additionally carried out the metallographic specimen allowing for counting grains. It can be concluded that the introduction of the iron powder significantly improved the number of austenite primary grains which resulted in an increase in tensile strength UTS.