The work deals with technology Patternless process that combines 3 manufacturing process mold by using rapid prototyping technology, conventional sand formation and 3D milling. It's unconventional technology that has been developed to produce large-sized and heavyduty castings weighing up to several tons. It is used mainly in prototype and small batch production, because eliminating production of models. The work deals with the production of blocks for making molds of gypsum and gypsum drying process technology Thermomold. Into blocks, where were made cavities by milling were casted test castings from AlSi10MgMn alloy by gravity casting. At machining of the mold cavity was varied feed rate of tool of cemented carbide. Evaluated was the surface roughness of test castings, that was to 5 micrometers with feed from 900 to 1300 mm/min. The dimensional accuracy of castings was high at feed rate of 1000 and 1500 mm/min did not exceed 0.025 mm.
The paper presents results of initial research on the possibility of applying microwave radiation in an innovative process of making casting moulds from silica sand, where gypsum CaSO4∙2H2O was acting as a binding material. In the research were compared strengths and technological properties of moulding mixture subjected to: natural bonding process at ambient temperature or natural curing with additional microwave drying or heating with the use of microwaves immediately after samples were formed. Used in the research moulding sands, in which dry constituents i.e. sand matrix and gypsum were mixed in the ratio: 89/11. On the basis of the results of strength tests which were obtained by various curing methods, beneficial effect of using microwaves at 2.45 GHz for drying up was observed after 1, 2 and 5 hours since moisture sandmix was formed. Applying the microwaves for hardening just after forming the samples guarantees satisfactory results in the obtained mechanical parameters. In addition, it has been noted that, from a technological and economic point of view, drying the silica sand with gypsum binder in microwave field can be an alternative to traditional molding sand technologies.
The dimensional accuracy of a final casting of Inconel 738 LC alloy is affected by many aspects. One of them is the choice of method and time of cooling the wax model for precision investment casting. The main objective of this work was to study the initial deformation of the complex shape of a rotor blades casting. Various approaches have been tested for cooling a wax pattern. When wax models are air cooled and without clamping in the jig for cooling, deviations from the ideal shape of the casting are very noticeable (up to 8 mm) and most are in extreme positions of the model. When the blade is cooled in the fixing jig in a water environment, the resulting deviations compared to those of air cooling are significantly larger, sometimes up to 10 mm. This itself does not mean that the final shape of the casting is dimensionally more accurate with the usage of wax models, which have smaller deviations from the ideal position. Another deformation occurs when the shell mould is produced around the wax pattern and further deformations emerge while cooling the blade casting. This paper demonstrates the first steps in describing the complex process of deformations occurring in Inconel alloy blades produced with investment casting technology by comparing results of thermal imagery, simulations in foundry simulation software ProCAST 2010, and measurements from a CNC scanning system using a Carl Zeiss MC 850. Conclusions are so far not groundbreaking, but it seems that deformations of the wax pattern and deformations of the castings do in some cases cancel each other by having opposite directions. Describing the whole process of deformations will help increase the precision of blade castings so that the models at the beginning and the blades in the end are the same.
The new investigation method of a permeability of ceramic moulds applied in the investment casting technology, is presented in the paper. Some concepts of performing permeability measurements are shown. Investigations in which the influence of the solid phase fraction in the liquid ceramic moulding sand (LCMS) on a permeability of a multi-layer ceramic mould were performed and discussed. The permeability was estimated during two the most important stages of the technological process: in the first – after wax melting and in the second – after mould annealing. Also an influence of the matrix grain sizes (material for sprinkling) on a ceramic mould permeability was estimated.
The paper describes existing requirements for tool materials. In the light of experience with these supplied materials, we have demonstrated their considerable influence on the life of molds for die casting technology. From this research came the evaluation methodology of these tool materials which has been used for directing the development of a new material. Based on the new regulation of the chemical composition a sample was casted and forged after that. Then was determined the process of heat treatment and from a block of this material a mold insert was produced. This insert is now being tested in production.
The purpose of the presented experiment was to develop an effective water glass modifier. In the conducted research, an attempt was made to determine the effect of modifier addition on the wettability of quartz grains, viscosity and cohesion of binder and strength Rm U of the sand mixture. Water glass modification was carried out with, obtained in electrochemical process , colloidal suspension of ZnO nanoparticles in methanol (modifier I) or propanol (modifier II), characterised by a constant molar concentration of c = 0.3 M. It was demonstrated that the addition of a colloidal suspension of ZnO nanoparticles in propanol (modifier II) had a significant effect on wettability of quartz grains improvement without the accompanying increase in binder viscosity. Testing the mechanical properties Rm U of sand mixtures containing modified binder (modifier II) hardened at ambient conditions showed an approximately 28% increase in strength compared with the Rm U of the sand bonded with an unmodified binder.
Owing to its properties, metallic foams can be used as insulation material. Thermal properties of cast metal-ceramic composite foams have applications in transport vehicles and can act as fire resistant and acoustic insulators of bulkheads. This paper presents basic thermal properties of cast and foamed aluminum, the values of thermal conductivity coefficient of selected gases used in foaming composites and thermal capabilities of composite foams (AlSi11/SiC). A certificate of non-combustibility test of cast aluminum-ceramic foam for marine applications was included inside the paper. The composite foam was prepared by the gas injection method, consisting in direct injection of gas into liquid metal. Foams with closed and open cells were examined. The foams were foaming with foaming gas consisting of nitrogen or air. This work is one of elements of researches connected with description of properties of composite foams. In author's other works acoustic properties of these materials will be presented.
The investigation results of the kinetics of binding ceramic moulds, in dependence on the solid phase content in the liquid ceramic slurries being 67, 68 and 69% - respectively, made on the basis of the aqueous binding agents Ludox AM and SK. The ultrasonic method was used for assessing the kinetics of strengthening of the multilayer ceramic mould. Due to this method, it is possible to determine the ceramic mould strength at individual stages of its production. Currently self-supporting moulds, which must have the relevant strength during pouring with liquid metal, are mainly produced. A few various factors influence this mould strength. One of them is the ceramic slurry viscosity, which influences a thickness of individual layers deposited on the wax model in the investment casting technology. Depositing of layers causes increasing the total mould thickness. Therefore, it is important to determine the drying time of each deposited layer in order to prevent the mould cracking due to insufficient drying of layers and thus the weakening of the multilayer mould structure.
A measuring system was developed for the measurement of ejector forces in the die casting process. When selecting the sensor technology, particular care was taken to ensure that measurements can be taken with a high sampling rate so that the fast-running ejection process can be recorded. For this reason, the system uses piezoelectric force sensors which measure the forces directly at the individual ejector pins. In this way, depending on the number of sensors, it is possible to determine both the individual ejector forces and the total ejector force. The system is expandable and adaptable with regard to the number and position of the sensors and can also be applied to real HPDC components. Automatic triggering of the measurements is also possible. In addition to the measuring system, a device and a method for in-situ calibration of the sensors have also been developed. To test the measuring system, casting experiments were carried out with a real aluminium HPDC aluminium component. The experiments showed that it is possible to measure the ejector forces with sufficient sampling rate and also to observe the process steps of filling, intensification and die opening by means of ejector forces. Experimental setup serves as a basis for future investigations regarding the influencing parameters on the ejection process.
This article presents a practical solution in the form of implementation of agent-based platform for the management of contracts in a network of foundries. The described implementation is a continuation of earlier scientific work in the field of design and theoretical system specification for cooperating companies . The implementation addresses key design assumptions - the system is implemented using multi-agent technology, which offers the possibility of decentralisation and distributed processing of specified contracts and tenders. The implemented system enables the joint management of orders for a network of small and medium-sized metallurgical plants, while providing them with greater competitiveness and the ability to carry out large procurements. The article presents the functional aspects of the system - the user interface and the principle of operation of individual agents that represent businesses seeking potential suppliers or recipients of services and products. Additionally, the system is equipped with a bi-directional agent translating standards based on ontologies, which aims to automate the decision-making process during tender specifications as a response to the request.