Paper presents the results of evaluation of heat resistance and specific heat capacity of MAR-M-200, MAR-M-247 and Rene 80 nickel superalloys. Heat resistance was evaluated using cyclic method. Every cycle included heating in 1100°C for 23 hours and cooling for 1 hour in air. Microstructure of the scale was observed using electron microscope. Specific heat capacity was measured using DSC calorimeter. It was found that under conditions of cyclically changing temperature alloy MAR-M-247 exhibits highest heat resistance. Formed oxide scale is heterophasic mixture of alloying elements, under which an internal oxidation zone was present. MAR-M-200 alloy has higher specific heat capacity compared to MAR-M-247. For tested alloys in the temperature range from 550°C to 800°C precipitation processes (γ′, γ′′) are probably occurring, resulting in a sudden increase in the observed heat capacity.
Grey cast iron belongs to materials for casting production, which have wide application for different industry branches. Wide spectrum of properties of these materials is given by the structure of base metal matrix, which can be influenced with heat treatment. Processes of annealing can be applied for grey cast iron without problems. During heat treatment processes, where higher cooling rates are used, the thermal and structural strains become important. Usage and conditions of such heat treatment for grey cast iron castings of common production are the subject of evaluation of this article.