Abstract

Mg60Zn35Ca5 amorphous powder alloys were synthesized by mechanical alloying (MA) technique. The results of the influence of high-energy ball-milling time on amorphization of the Mg60Zn35Ca5 elemental blend (intended for biomedical application) were presented in the study. The amorphization process was investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM). Initial elemental powders were mechanically alloyed in a Spex 8000 high-energy ball mill at different milling times (from 3 to 24 h). Observation of the powder morphology after various stages of milling leads to the conclusion that with the increase of the milling time the size of the powder particles as well as the degree of aggregation change. The partially amorphous powders were obtained in the Mg60Zn35Ca5 alloy after milling for 13-18h. The results indicate that this technique is a powerful process for preparing Mg60Zn35Ca5 alloys with amorphous and nanocrystalline structure.
Go to article

Abstract

It is assumed that close to the margins of ice-sheets, glacial, fluvial and aeolian processes overlap, and combined with weathering processes, produce numerous sediments, in which quartz is a common mineral. Quartz grains, if available, may serve as a powerful tool in determining the depositional history, transportation mode and postdepositional processes. However, quartz grain studies in some modern glacial areas are still sparse. In this study, we examine for the first time quartz grains sampled from the modern glacial and proglacial environments of the Russell Glacier, southwest Greenland in binocular microscope and scanning electron microscope, to analyze their shape, character of surface and microtextures. We debate whether the investigated quartz grains reveal glacial characteristics and to what extent they carry a signal of another transportation and sedimentary processes. Although glacial fracturing and abrasion occur in grain suites, most mechanical origin features are not of a high frequency or freshness, potentially suggesting a reduced shear stress in the glacier from its limited thickness and influence of the pressurized water at the ice-bed. In contrast, the signal that originates from the fluvial environment is much stronger derived by numerous aqueous-induced features present on quartz grain surfaces. Aeolian-induced microtextures on grain surfaces increase among the samples the closest to the ice margin, which may be due to enhanced aeolian activity, but are practically absent in sediments taken from the small scale aeolian landforms. In contrast, aeolian grains have been found in the bigger-size (1.0-2.0 mm) investigated fraction. These grains gained the strongest aeolian abrasion, possibly due to changes in transportation mode.
Go to article

Abstract

The technique of electrospinning was employed to fabricate uniform one-dimensional inorganic-organic composite nanofibers at room temperature from a solution containing equal volumes of aluminum 2, 4-pentanedionate in acetone and polyvinylpyrrolidone in ethanol. Upon firing and sintering under carefully pre-selected time-temperature profiles (heating rate, temperature and soak time), high-purity and crystalline alumina nanofibers retaining the original morphological features present in the as-spun composite (cermer) fibers were obtained. Tools such as laser Raman spectroscopy, scanning and transmission electron microscopy together with energy dispersive spectroscopy and selected area electron diffraction were employed to follow the systematic evolution of the ceramic phase and its morphological features in the as-spun and the fired fibers. X-ray diffraction was used to identify the crystalline fate of the final product.
Go to article

Abstract

An equiatomic multi-component alloy Ni20Ti20Ta20Co20Cu20 (at. %) was obtained using vacuum arc melting. In order to characterize such an alloy, microstructure analysis has been performed using Scanning and Transmission Electron Microscopy, Electron Backscattered Diffraction, X-ray Diffraction and Energy Dispersive X-ray Spectroscopy techniques. Microstructure analysis revealed the presence of one rhombohedral and two cubic phases. Energy Dispersive X-ray Spectroscopy measurements revealed that both observed phases include five chemical elements in the structure. Using Rietveld refinement approach the lattice parameters were refined for the observed phases.
Go to article

Abstract

A new NiTi-based multi-component Ni35Ti35Ta10Co10Cu10 (at.%) alloy was obtained by vacuum arc melting. The microstructure of the alloy has been studied using scanning and transmission electron microscopy, backscatter electron diffraction and X-ray diffraction techniques. The performed measurements showed presence of two cubic and one tetragonal phases. Energy dispersive X-ray spectroscopy analysis confirmed that all the observed phases contained all five principal elements.
Go to article

Abstract

The knowledge whether and how chemical species react with tissues is important because of protection against harmful factors, diagnose of dermatological diseases, validation of dermatological procedures as well as effectiveness of topical therapies. In presented work the effects of chemical agents on plates of human fingernails were studied using Atomic Force Microscopy and Scanning Electron Microscopy. Apart from that, mapping of the elastic properties of the nails was also carried out. To obtain reliable measures of spatial evolution of the surface variations, recorded images were analyzed in terms of scaling invariance brought by fractal geometry, instead of common though not unique statistical measures.
Go to article

Abstract

The aim of this work was to investigate the possibility of obtaining an amorphous/crystalline composite starting from Ni-Si- B-based powder grade 1559-40 and silver powder. The alloy was produced using arc melting of 95% wt. Ni-Si-B-based powder (1559-40) and 5% wt. Ag powder. Ingot was re-melted on a copper plate and observed while cooling using a mid-wave infra-red camera. The alloy was then melt-spun in a helium atmosphere. The microstructure of the ingot as well as the melt-spun ribbon was studied using light microscopy and scanning electron microscopy with energy dispersive spectrometry. Phase identification was performed by means of X-ray diffraction. The observations confirmed an amorphous/crystalline microstructure of the ribbon where the predominant constituent of the microstructure was an amorphous phase enriched with Ni, Si, and B, while the minor constituent was an Ag-rich crystalline phase distributed in a film along the melt-spinning direction.
Go to article

Abstract

In this work, vacuum hot pressed Ni-Mn-Sn-In Heusler alloys with different concentration of In (0, 2 and 4 at.%), were investigated. The magneto-structural behaviour and microstructure dependencies on chemical composition and on heat treatment were examined. It was found that the martensite start transformation temperature increases with growing In content and to a lesser extent with increasing temperature of heat treatment. The high energy X-ray synchrotron radiation results, demonstrated that both chemical composition as well as temperature of heat treatment slightly modified the crystal structures of the studied alloys. Microstructural investigation performed by transmission electron microscopy confirmed chemical composition and crystal structure changes in the alloys.
Go to article