The effects of silica additive (Poraver) on selected properties of BioCo3 binder in form of an aqueous poly(sodium acrylate) and dextrin (PAANa/D) binder were determined. Based on the results of the thermoanalytical studies (TG-DTG, FTIR, Py-GC/MS), it was found that the silica additive results in the increase of the thermostability of the BioCo3 binder and its contribution does not affect the increase in the level of emissions of organic destruction products. Compounds from group of aromatic hydrocarbons are only generated in the third set temperature range (420-838°C). The addition of silicate into the moulding sand with BioCo3 causes also the formation of a hydrogen bonds network with its share in the microwave radiation field and they are mainly responsible for maintaining the cross-linked structures in the mineral matrix system. As a consequence, the microwave curing process in the presence of Poraver leads to improved strength properties of the moulding sand (���� �� ). The addition of Poraver's silica to moulding sand did not alter the permeability of the moulding sand samples, and consequently reduced their friability. Microstructure investigations (SEM) of microwave-cured samples have confirmed that heterogeneous sand grains are bonded to one another through a binder film (bridges).
This publication describes research on the course of the process of cross-linking new BioCo polymer binders - in the form of water-based polymer compositions of poly(acrylic acid) or poly(sodium acrylate)/modified polysaccharide - using selected physical and chemical factors. It has been shown that the type of cross-linking factor used influences the strength parameters of the moulding sand. The crosslinking factors selected during basic research make it possible to obtain sand strengths similar to those of samples of sands bonded with commercial binders. Microwave radiation turned out to be the most effective cross-linking factor in a binder-matrix system. It was proven that adsorption in the microwave radiation field leads to the formation of polymer lattices with hydrogen bonds which play a major role in maintaining the formed cross-linked structures in the binder-matrix system. As a result, the process improves the strength parameters of the sand, whereas the hardening process in a microwave field significantly shortens the setting time.
In this paper the results of studies of polymeric binders on the example of the new BioCo2 binder, including the problem of its renewability, are presented. The results of structural studies (FT-IR) for the BioCo2 binder before and after crosslinking, and bending strength tests Rg u fresh and renewed cured molding sands with BioCo2 binder are discussed. The cross-linking binder and curring of moulding sand was carried out by physical agents (microwave radiation, temperature). On the basis of obtained results was shown that it is possible to restore the initial properties of the adhesive of BioCo2 binder. The initial properties of moulding sand can be achieved, after the cross-linking binders and after curing in the moulding sands with bioCo2 binder , by supplementing the moulding sand composition by the appropriate amount of water.
The spectroscopic FT-IR and FT-Raman methods allowed to identify the cross-linking process of the aqueous composition of poly(acrylic acid)/sodium salt of carboxymethyl starch (PAA/CMS-Na) applied as a binder for moulding sands (as a novel group binders BioCo). The cross-linking was performed by physical agent, applying the UV-radiation. The results of structural studies (IR, Raman) confirm the overlapping of the process of cross-linking polymer composition PAA/CMS-Na in UV radiation. Taking into account the ingredients and structure of the polymeric composition can also refer to a curing process in a binder - mineral matrix mixture. In the system of bindermineral matrix under the influence of ultraviolet radiation is also observed effect of binding. However, the bonding process does not occur in the entire volume of the investigated system, but only on the surface, which gives some possibilities for application in the use of UV curing surface of cores, and also to cure sand moulds in 3D printing technology
The ethylene vinyl acetate (EVA) is widely used for solar modules encapsulation. During lamination process EVA melts and chemical bonds between polymer chains are created. Its number is tightly related to cross-linking degree and it is consider as a major quality reference for module encapsulation. The lamination can be described as a process with two stages: melting and curing where the typical temperature for curing is in the range from 145 to 175°C. In the present study, for the first time, comparison of three commercial available EVA foils with low curing temperature EVA (EVA LOW). For this reason, the temperature of following lamination processes was set from a range from 115 to 175°C. The behavior of cured EVA films under investigation EVA was determined with two approaches: with extraction and with optical methods. The results indicate the applicability of these methods for the EVA cross-linking characterization. Finally, the extraordinary behavior of EVA LOW foil was noticed.