The paper presents the method of preparing a composite slurry composed of AlSi11 alloy matrix and 10 vol.% of SiC particles, as well as the method of its high-pressure die casting and the measurement results concerning the castability of the obtained composite. Composite castings were produced at various values of the piston velocity in the second stage of injection, diverse intensification pressure values, and various injection gate width values. There were found the regression equations describing the change of castability of the examined composite as a function of pressure die casting process parameters. The conclusion gives the analysis and the interpretation of the obtained results.
The results of castability and structures researches of two nickel base alloys - Ceranium CN and Magnum AN applied on casting of the crowns and dental bridges are presented. Studies were carried out on the alloys cast under the centrifugal force to the moulds made by the lost wax method using production line of ROKO. Having regard to a specific technology of casting and possibility of ROKO production line, to the estimation of alloys castability a spiral test was adjusted with a 0,8 mm and a 2,5 mm diameter of test casting. Measuriements executed on a 20 test castings allowed to establish, that castability of Magnum AN alloy was 65 % greater than castability of Ceranium NC alloy. The results of thermodynamics calculations of the equilibrium and nonequilibrium crystallization (Scheil model) of the investigated alloys are presented too. The characteristic temperatures of phase transformation and forecast phase composition of alloys for both kind of crystallization were calculated. It is established after structural supervisions, that the investigated alloys crystallize in dendryte form and in centrifugal casting conditions have cooling rate sensivity and inclination to texture structure forming in outmost layer of casting. Phase composition of alloys corresponds to the results of thermodynamics calculations of the nonequilibrium crystallization conditions.
This paper presents the results of measurements of liquid metal fluidity and linear shrinkage of nickel alloy IN-713C in vacuum induction melting furnace Balzers VSG-2. Because of limited volume of the furnace chamber special models for technological trials were designed and constructed to fit in the mould of dimensions 170x95x100mm. Two different designs of test models were proposed: horizontal round rods and modified spiral. Preliminary studies were carried out for alloys Al-Si. Horizontal round rods test was useful for evaluation of fluidity of hypoeutectic silumin, however in case of nickel superalloy the mould cavity was completely filled in each test because of high required pouring temperature. Positive results were obtained from the modified spiral test for all alloys used in the research. Relationship between the linear shrinkage for the test rod and a specific indicator of contraction defined on a spiral was observed.