Number of results: 18
items per page: 25 50 75
Sort by:

Abstract

The paper presents results of bend tests at elevated temperatures of aluminium alloy EN AC-44200 (AlSi12) based composite materials reinforced with aluminium oxide particles. The examined materials were manufactured by squeeze casting. Preforms made of Al2O3 particles, with volumetric fraction 10, 20, 30 and 40 vol.% of particles joined with sodium silicate bridges were used as reinforcement. The preforms were characterised by open porosity ensuring proper infiltration with the EN AC-44200 (AlSi12) liquid alloy. The largest bending strength was found for the materials containing 40 vol.% of reinforcing ceramic particles, tested at ambient temperature. At increased test temperature, bending strength Rg of composites decreased in average by 30 to 50 MPa per 100°C of temperature increase. Temperature increase did not significantly affect cracking of the materials. Cracks propagated mainly along the interfaces particle/matrix, with no effect of the particles falling-out from fracture surfaces. Direction of cracking can be affected by a small number of agglomerations of particles or of non-reacted binder. In the composites, the particles strongly restrict plastic deformation of the alloy, which leads to creation of brittle fractures. At elevated temperatures, however mainly at 200 and 300°C, larger numbers of broken, fragmented particles was observed in the vicinity of cracks. Fragmentation of particles occurred mainly at tensioned side of the bended specimens, in the materials with smaller fraction of Al2O3 reinforcement, i.e. 10 and 20 vol.%.
Go to article

Abstract

The paper deals with the impact of technological parameters on the heat transfer coefficient and microstructure in AlSi12 alloy using squeeze casting technology. The casting with crystallization under pressure was used, specifically direct squeeze casting method. The goal was to affect crystallization by pressure with a value 100 and 150 MPa. The pressure applied to the melt causes a significant increase of the coefficient of heat transfer between the melt and the mold. There is an increase in heat flow by approximately 50% and the heat transfer coefficient of up to 100-fold, depending on the casting conditions. The change in cooling rate influences the morphology of the silicon particles and intermetallic phases. A change of excluded needles to a rod-shaped geometry with significantly shorter length occurs when used gravity casting method. By using the pressure of 150 MPa during the crystallization process, in the structure can be observed an irregular silica particles, but the size does not exceed 25 microns.
Go to article

Abstract

The paper deals with the impact of technological parameters on the mechanical properties and microstructure in AlSi12 alloy using squeeze casting technology. The casting with crystallization under pressure was used, specifically direct squeeze casting method. The goal was to affect crystallization by pressure with a value 100 and 150 MPa. From the experiments we can conclude that operating pressure of 100 MPa is sufficient to influence the structural characteristics of the alloy AlSi12. The change in cooling rate influences the morphology of the silicon particles and intermetallic phases. A change of excluded needles to a rod-shaped geometries with significantly shorter length occurs when used gravity casting method. At a pressure of 100 MPa was increased of tensile strength on average of 20%. At a pressure of 150 MPa was increased of tensile strength on average of 30%. During the experiment it was also observed, that increasing difference between the casting temperature and the mold temperature leads to increase of mechanical properties.
Go to article

Abstract

The article discusses the weldment to casting conversion process of rocker arm designed for operation in a special purpose vehicle to obtain a consistency of objective functions, which assume the reduced weight of component, the reduced maximum effort of material under the impact of service loads achieved through topology modification for optimum strength distribution in the sensitive areas, and the development of rocker arm manufacturing technology. As a result of conducted studies, the unit weight of the item was reduced by 25%, and the stress limit values were reduced to a level guaranteeing safe application.
Go to article

Abstract

Magnesium alloy with 5 wt% Al, 0.35 wt% Mn and 5 wt% rare earth elements (RE) was prepared and gravity cast into a sand mould. Microstructure investigations were conducted. Analyses of the Mg-Al-RE alloy microstructure were carried out by light microscopy, scanning electron microscopy and the XRD technique. In the as-cast condition, the alloy was composed of α-Mg, Al11RE3 and Al10RE2Mn7 intermetallic phases. Additionally, due to non-equilibrium solidification conditions, an Al2RE intermetallic phase was revealed.
Go to article

Abstract

The article presents the analysis of properties of the high-strength AlZnMgCu (abbr AlZn) aluminium alloy and estimates possibilities of its application for responsible structures with reduced weight as an alternative to iron alloy castings. The aim of the conducted studies was to develop and select the best heat treatment regime for a 7xx casting alloy based on high-strength materials for plastic working from the 7xxx series. For analysis, wrought AlZnMgCu alloy (7075) was selected. Its potential of the estimated as-cast mechanical properties indicates a broad spectrum of possible applications for automotive parts and in the armaments industry. The resulting tensile and fatigue properties support the thesis adopted, while the design works further confirm these assumptions.
Go to article

Abstract

The research described in this contribution is focused on fractographic analysis of the fracture area of newly developed eutectic silumin type AlSi9NiCuMg0.5 (AA 4032), which was developed and patented by a team of staff of the Faculty of Mechanical Engineering. The paper presents determination of the cause of casting cracks in operating conditions. Fractographic analysis of the fracture area, identification of the structure of the casting, identification of structural components on the surface of the fracture surface and chemical analysis of the material in the area of refraction were performed within the experiment. Al-Si alloys with high specific strength, low density, and good castability are widely used in pressure-molded components for the automotive and aerospace industries. The results shown that the inter-media phases Fe-Al and Fe-Si in aluminium alloys lead to breakage across the entire casting section and a crack that crossed the entire cross section, which was confirmed by EDS analysis.
Go to article

Abstract

The paper presents research on the effects of soft annealing parameters on a change of the impact strength KC and Brinell hardness (HB) of the EN AC-AlSi11 alloy. The research has been performed according to the trivalent testing plan for two input parameters – temperature in the range between 280°C and 370°C and time in the range between 2 and 8 hours. The application of such heat treatment improves the plasticity of the investigated alloy. The improvement of the impact strength KC by 71% and the decrease of the hardness HB by 20% was achieved for the soft annealing treatment conducted at a temperature 370°C for 8 hours, compared to the alloy without the heat treatment. A change of the form of eutectic silicon precipitations which underwent refinement, coagulation and partial rounding, had a direct effect on the hardness HB and impact strength KC. The results obtained were used to prepare space plots enabling the temperature and time for soft annealing treatment to be selected with reference to the obtained impact strength KC and hardness HB of the alloy with the heat treatment.
Go to article

Abstract

The article presents the effect of rotational and travelling speed and down force on the spindle torque acting on the tool in Friction Stir Processing (FSP) process. The response surface methodology (RSM) was applied to find a dependence combining the spindle torque acting on the tool with the rotational speed, travelling speed and the down force. The linear and quadratic models with interaction between parameters were used. A better fitting was achieved for a quadratic model. The studies have shown that the increase in rotational speed causes a decrease in the torque while the increase in travelling speed and down force causes an increase in the torque. The tests were conducted on casting aluminium alloy AlSi9Mg. Metallography examination has revealed that the application of FSP process results in a decrease in the porosity in the modified material and microstructure refining in the stir zone. The segregation of Si and Fe elements was evident in the parent material, while in the friction stir processed area this distribution was significantly uniform.
Go to article

Abstract

A comprehensive understanding of melt quality is of paramount importance for the control and prediction of actual casting characteristics. Among many phenomenon that occur during the solidification of castings, there are four that control structure and consequently mechanical properties: chemical composition, liquid metal treatment, cooling rate and temperature gradient. The cooling rate and alloy composition are most important among them. This paper investigates the effect of the major alloying elements (silicon and copper) of AlSi-Cu alloys on the size of secondary dendrite arm spacing. It has been shown that both alloying elements have reasonable influence on the refinement of this solidification parameter
Go to article

Abstract

This paper describes the possibility of using very short periods of solution annealing in the heat treatment of unmodified hypoeutectic silumin alloy AlSi7Mg0,3 casted by method of casting with crystallization under pressure with forced convection (direct squeeze casting process). Castings prepared at different casting parameters were subjected to special heat treatment called SST (Silicon Spheroidization Treatment), which were originally used only for the modified silumin alloys to spheroidization of eutectic silicon. Temperature holding time in solution annealing of T6 heat treatment is limited in the SST process to only a few minutes. It was studied the effect of casting parameters and periods of solution annealing on ultimate strength, yield strength, and especially ductility that in the unmodified silumin alloy castings is relatively low.
Go to article

Abstract

US A356 and US 413 cast aluminium alloys shrinkage characteristic have been discussed in the present study. Specific volume reduction leads to shrinkage in castings and it can be envisaged as a casting defect. Finite difference based casting process simulation software has been used to study the shrinkage characteristic and it is quantified using mathematical formulae. The three dimensional model of the shrinkage defect has been constructed using CAD application software. Shrinkage characteristic has also been quantified through experimental validation studies and compared well with casting process simulation. Shrinkage characteristic study and control is essential for producing defect free castings. Influence of casting shape on the shrinkage characteristic has been studied in this paper.
Go to article

Abstract

Ceramic injection moulding and gas pressure infiltration were employed for the manufacturing of alumina/AlSi10Mg composites. Porous ceramic preforms were prepared by mixing alumina powder with a multi-binder system and injection moulding of the powder polymer slurry. Then, the organic part was removed through a combination of solvent and thermal debinding, and the materials were finally sintered at different temperatures. The ceramic preforms manufactured in this way were infiltrated by an AlSi10Mg alloy. The microstructure and properties of the manufactured materials were examined using scanning electron microscopy, mercury porosimetry and bending strength testing. The results of transmission electron microscopy and scanning electron microscopy observations show that the fabricated composite materials are characterised by the percolation type of the microstructure and a lack of unfilled pores with good cohesion at the metal-ceramic interfaces. This is surprising considering that over 30% of the pores are smaller than 1 μm. The results show that the bending strength of the obtained composites decreased with increasing sintering temperature of the porous preforms.
Go to article

Abstract

The work deals with technology Patternless process that combines 3 manufacturing process mold by using rapid prototyping technology, conventional sand formation and 3D milling. It's unconventional technology that has been developed to produce large-sized and heavyduty castings weighing up to several tons. It is used mainly in prototype and small batch production, because eliminating production of models. The work deals with the production of blocks for making molds of gypsum and gypsum drying process technology Thermomold. Into blocks, where were made cavities by milling were casted test castings from AlSi10MgMn alloy by gravity casting. At machining of the mold cavity was varied feed rate of tool of cemented carbide. Evaluated was the surface roughness of test castings, that was to 5 micrometers with feed from 900 to 1300 mm/min. The dimensional accuracy of castings was high at feed rate of 1000 and 1500 mm/min did not exceed 0.025 mm.
Go to article

Abstract

The study presents the results of the investigations of the effect of Cu, Ni, Cr, V, Mo and W alloy additions on the microstructure and mechanical properties of the AlSi7Mg0.3 alloy. The examinations were performed within a project the aim of which is to elaborate an experimental and industrial technology of producing elements of machines and devices complex in their construction, made of aluminium alloys by the method of precision investment casting. It was demonstrated that a proper combination of alloy additions causes the crystallization of complex intermetallic phases in the silumin, shortens the SDAS and improves the strength properties: Rm, Rp0.2,HB hardness. Elevating these properties reduces At, which, in consequence, lowers the quality index Q of the alloy of the obtained casts. Experimental casts were made in ceramic moulds preliminarily heated to 160 °C, into which the AlSi7Mg0.3 alloy with the additions was cast, followed by its cooling at ambient temperature. With the purpose of increasing the value of the quality index Q, it is recommended that the process of alloy cooling in the ceramic mould be intensified and/or a thermal treatment of the casts be performed (ageing)(T6).
Go to article

Abstract

The work presents the investigation results concerning the structure of composite pressure die castings with AlSi11 alloy matrix reinforced with SiC particles. Examination has been held for composites containing 10 and 20 volume percent of SiC particles. The arrangement of the reinforcing particles within the matrix has been qualitatively assessed in specimens cut out of the castings. The index of distribution was determined on the basis of particle count in elementary measuring fields. The tensile strength, the yield point and elongation of the obtained composite were measured. Composite castings were produced at various values of the piston velocity in the second stage of injection, diverse intensification pressure values, and various injection gate width values. The regression equation describing the change of the considered arrangement particles index and mechanical properties were found as a function of the pressure die casting parameters. The infuence of particle arrangement in composite matrix on mechanical properties these material was examined and the functions of correlations between values were obtained. The conclusion gives the analysis and the interpretation of the obtained results.
Go to article