Abstract

In the paper, a research on effects of baking temperature on chromite sand base of moulding sands bonded with sodium silicate is presented. Pure chromite sand and its chromite-based moulding sand prepared with use of sodium silicate were subjected to heating within 100 to 1200 °C. After cooling-down, changes of base grains under thermal action were determined. Chromite moulding sand was prepared with use of 0.5 wt% of domestic made, unmodified sodium silicate (water-glass) grade 145. After baking at elevated temperatures, creation of rough layer was observed on grain surfaces, of both pure chromite sand and that used as base of a moulding sand. Changes of sand grains were evaluated by scanning microscopy and EDS analyses. It was found that changes on grain surfaces are of laminar nature. The observed layer is composed of iron oxide (II) that is one of main structural components of chromite sand. In order to identify changes in internal structure of chromite sand grains, polished sections were prepared of moulding sand hardened with microwaves and baked at elevated temperatures. Microscopic observations revealed changes in grains structure in form of characteristically crystallised acicular particles with limited magnesium content, intersecting at various angles. EDS analysis showed that these particles are composed mostly of chromium oxide (III) and iron oxide (II). The temperature above that the a.m. changes are observed in both chromite-based moulding sand and in pure chromite sand. The observed phenomena were linked with hardness values and mass of this sand.
Go to article

Abstract

Railway buffers during the operation are staying in almost permanent contact with each other, creating friction node in the point of contact of two railway buffer heads. In consequence of overcoming track curves, turnouts and unevenness of track, the railway buffer heads moves relative to each other causing friction, which results in its wear. When the wear is excessive, it might be a reason to withdrawn vehicle from service, it causes flattening of buffer head, and in consequence its abnormal cooperation. To avoid this phenomenon the buffer heads should be covered with graphitized grease, but this method has many disadvantages. Accordingly, it was found that it would be beneficial to cover the buffer head with bronze using laser cladding. In this article the metallographic and mechanical analysis of the newly created top layer of railway buffer head are presented. In article the results from tribological tests conducted on Amsler test bench are also presented. Based on test results described in article concluded that the layer of bronze coat on working surface of railway buffer head can be beneficial from operational point of view.
Go to article

Abstract

The aim of research was creation of a furnace for aluminum alloys smelting “in a liquid bath” in order to reduce metal loss. In the paper, the author demonstrates the results of research on smelting of aluminum alloys in a shaft-reverberatory furnace designed by the author. It has been shown that smelting aluminum alloy in a liquid bath was able to significantly reduce aluminum loss and that shaft-reverberatory design provided high efficiency and productivity along with lower energy costs. Ensuring continuous operation of the liquid bath and superheating chamber, which tapped alloy with the required texture, was achieved by means of the optimal design of partition between them. The optimum section of the connecting channels between the liquid bath of smelting and the superheating chamber has been theoretically substantiated and experimentally confirmed. The author proposed a workable shaft-reverberatory furnace for aluminum alloys smelting, providing solid charge melting in a liquid bath.
Go to article

Abstract

The paper presents the research results of horizontal continuous casting of ingots of aluminium alloy containing 2% wt. silicon (AlSi2). Together with the casting velocity (velocity of ingot movement) we considered the influence of electromagnetic stirring in the area of the continuous casting mould on refinement of the ingot’s primary structure and their selected mechanical properties, i.e. tensile strength, yield strength, hardness and elongation. The effect of primary structure refinement and mechanical properties obtained by electromagnetic stirring was compared with refinement obtained by using traditional inoculation, which consists in introducing additives, i.e. Ti, B and Sr, to the metal bath. On the basis of the obtained results we confirmed that inoculation done by electromagnetic stirring in the range of the continuous casting mould guarantees improved mechanical properties and also decreases the negative influence of casting velocity, thus increasing the structure of AlSi2 continuous ingots.
Go to article

Abstract

The article deals with ultrasonic testing possibilities of the copper alloy centrifugal casts. It focused on the problems that arise when testing of castings is made of non-ferrous materials. Most common types of casting defects is dedicated in theoretical introduction of article. Ultrasonic testing technique by conventional ultrasound system is described in the theoretical part too. Practical ultrasonic testing of centrifugal copper alloy cast - brass is in experimental part. The experimental sample was part of centrifugally cast brass ring with dimensions of Ø1200x34 mm. The influence of microstructure on ultrasonic attenuation and limitations in testing due to attenuation is describes in experimental part. Conventional direct single element contact ultrasound probe with frequencies of 5 MHz, 3.5 MHz and 2 MHz were used for all experimental measurements. The results of experimental part of article are recommendations for selecting equipment and accessories for casting testing made of non-ferrous metals.
Go to article

Abstract

Within the research, selected multilayer technological systems created as combinations of water-glass containing moulding sand with foundry tooling, were characterised on the grounds of their electrical properties. By measuring resonance frequency and quality factor of a waveguide resonance cavity, real component of permittivity εr′ and loss tangent tgδ were determined for multilayer foundry systems with various qualitative and quantitative compositions. It was demonstrated that combination of a sandmix and foundry tooling with known dielectric properties results in a system with different physico-chemical properties, whose relation to the parameters of individual components of the system is undefined at this research stage. On the grounds of measurement results, theoretical value of microwave heating power, dissipated in unit volume of the selected multilayer foundry system, was determined. Knowledge of theoretical heating power and evaluation of physical, chemical and structural changes occurring in moulding sands exposed to microwaves in such a technological system makes a ground for empirical modelling of the process of microwave heating of foundry moulds and cores.
Go to article

Abstract

The rebuilding technologies are used to develop surface of ladle. Among many welding methods currently used to obtain surface layer without defects one of the most effective way of rebuilding is using metal arc welding. This additional material gives more possibilities to make expected quality of rebuild surface. Chemical composition, property and economic factors allow to use metal wire. Because of these reasons, solid wire gives opportunity to be wildly used as material to rebuild or repair the surface in different sectors of industry. The paper shows a few ways to rebuild the surface in the massive cast with the use of metal active gas welding for repair. The work presents studies of defect in the massive cast. It contains the pictures of microstructures and defects. The method of removing defects and the results of checking by visual and penetrant testing methods are shown. The paper describes the methodology of repair the ladle with metal active gas welding, preheating process and standards nondestructive testing method.
Go to article

Abstract

The paper deals with the impact of technological parameters on the heat transfer coefficient and microstructure in AlSi12 alloy using squeeze casting technology. The casting with crystallization under pressure was used, specifically direct squeeze casting method. The goal was to affect crystallization by pressure with a value 100 and 150 MPa. The pressure applied to the melt causes a significant increase of the coefficient of heat transfer between the melt and the mold. There is an increase in heat flow by approximately 50% and the heat transfer coefficient of up to 100-fold, depending on the casting conditions. The change in cooling rate influences the morphology of the silicon particles and intermetallic phases. A change of excluded needles to a rod-shaped geometry with significantly shorter length occurs when used gravity casting method. By using the pressure of 150 MPa during the crystallization process, in the structure can be observed an irregular silica particles, but the size does not exceed 25 microns.
Go to article

Abstract

The paper presents the production problems related to casting using precision casting methods. The essential adverse effect of the casting process is the presence of burrs understood as oversize material necessary to remove the next finishing operations. In addition, the surfaces of the cast often characterized by a porous structure. One of the methods to improve the smoothness of the area proposed by the authors is the use of vibro-abrasive finishing. This type of treatment is widely used in the treatment of finishing small objects as well as complex shapes. Objects in the form of casting in the first step was treated with aggressive deburring polyester matrix abrasive media. The second stage was polishing, with using smoothing porcelain media. The study evaluated the effect of vibro-abrasive machining typical cast on the basic parameters of the geometric structure of the surface. Observations using optical microscope Nicon Eclipse MA 200 compared changes in surface microstructure and the effect of deburring. Clearly we can say that vibro-abrasive machining an effective way of reducing the size of burrs, smoothing and lightening the surface of objects made by casting.
Go to article

Abstract

It is well-known that the better the control of the liquid aluminium allows obtaining of better properties. One of the most important defects that is held responsible for lower properties has been the presence of porosity. Porosity has always been associated with the amount of dissolved hydrogen in the liquid. However, it was shown that hydrogen was not the major source but only a contributor the porosity. The most important defect that causes porosity is the presence of bifilms. These defects are surface entrained mainly due to turbulence and uncontrolled melt transfer. In this work, a cylindrical mould was designed (Ø30 x 300 mm) both from sand and die. Moulds were produced both from sand and die. Water cooled copper chill was placed at the bottom of the mould in order to generate a directional solidification. After the melt was prepared, prior to casting of the DC cast samples, reduced pressure test sample was taken to measure the melt quality (i.e. bifilm index). The cast parts were then sectioned into regions and longitudinal and transverse areas were investigated metallographically. Pore size, shape and distribution was measured by image analysis. The formation of porosity was evaluated by means of bifilm content, size and distribution in A356 alloy.
Go to article

Abstract

The article presents crystallization process of silicon molybdenum ductile cast iron (SiMo). The alloy with 5% silicon content and with variable amounts of Mo in a range of 0-1% was chosen for the research. The carbon content in the analysed alloys did not exceed 3,1%. The studies of crystallization process were based on thermal – derivative analysis (TDA). Chemical composition of all examined samples was analysed with the use of LECO spectrometer. Additionally, the carbon and the sulphur content was determined basing on carbon and sulphur LECO analyser. For metallographic examination, the scanning electron microscopy (SEM) with EDS analyser was used. Disclosed phases have been also tested with the use of X-ray diffraction. The results allowed the description of crystallization processes of silicon molybdenum ductile cast iron using thermal – derivative analysis (TDA). Conducted studies did not allow for the clear identification of all complex phases containing molybdenum, occurring at the grain boundaries. Therefore, the further stages of the research could include the use of a transmission electron microscope to specify the description of complex compounds present in the alloy.
Go to article

Abstract

Wear resistance of TiC-cast steel metal matrix composite has been investigated. Composites were obtained with SHSB method known as SHS synthesis during casting. It has been shown the differences in wear between composite and base cast steel. The Miller slurry machine test were used to determine wear loss of the specimens. The slurry was composed of SiC and water. The worn surface of specimens after test, were studied by SEM. Experimental observation has shown that surface of composite zone is not homogenous and consist the matrix lakes. Microscopic observations revealed the long grooves with SiC particles indented in the base alloy area, and spalling pits in the composite area. Due to the presence of TiC carbides on composite layer, specimens with TiC reinforced cast steel exhibited higher abrasion resistance. The wear of TiC reinforced cast steel mechanism was initially by wearing of soft matrix and in second stage by polishing and spalling of TiC. Summary weight loss after 16hr test was 0,14÷0,23 g for composite specimens and 0,90 g for base steel
Go to article

Abstract

The paper presents an analysis of the effect of shape of primary silicon crystals on the sizes of stresses and deformations in a surface layer of A390.0 alloy by Finite Elements Method (FEM). Analysis of stereological characteristics of the studied alloy, performed based on a quantitative metallographic analysis in combination with a statistical analysis, was used for this purpose. The presented simulation tests showed not only the deposition depth of maximum stresses and strains, but also allowed for determining the aforementioned values depending on the shape of the silicon crystals. The studied material is intended for pistons of internal combustion engines, therefore the analysis of the surface layer corresponded to conditions during friction in a piston-cylinder system of an internal combustion engine having power of up to 100 kW. The obtained results showed important differences in the values of stresses and strains up to 15% between various shape of the silicon crystals. Crystals with sharp edges caused higher stresses and deformation locally than those with rounded shapes.
Go to article

Abstract

This paper focuses on mechanical properties of self hardening moulding sands with furfuryl and alkyd binders. Elasticity as a new parameter of moulding sands is investigated. With the use of presented testing equipment, it is possible to determine force kinetics and deformation of moulding sand in real time. The need for this kind of study comes from the modern casting industry. New foundries can be characterized with high intensity of production which is correlated with high level of mechanization and automatization of foundry processes. The increasingly common use of manipulators in production of moulds and cores can lead to generation of new types of flaws, caused by breakage in moulds and cores which could occur during mould assembly. Hence it is required that moulds and cores have high resistance to those kinds of factors, attributing it with the phenomenon of elasticity. The article describes the theoretical basis of this property, presents methods of measuring and continues earlier research.
Go to article

Abstract

This paper deals with computer modelling of the retention of a synthetic diamond particle in a metallic matrix produced by powder metallurgy. The analyzed sintered powders can be used as matrices for diamond impregnated tools. First, the behaviour of sintered cobalt powder was analyzed. The model of a diamond particle embedded in a metallic matrix was created using Abaqus software. The preliminary analysis was performed to determine the mechanical parameters that are independent of the shape of the crystal. The calculation results were compared with the experimental data. Next, sintered specimens obtained from two commercially available powder mixtures were studied. The aim of the investigations was to determine the influence of the mechanical and thermal parameters of the matrix materials on their retentive properties. The analysis indicated the mechanical parameters that are responsible for the retention of diamond particles in a matrix. These mechanical variables have been: the elastic energy of particle, the elastic energy of matrix and the radius of plastic zone around particle.
Go to article

Abstract

Paper presents the results of ATD and DSC analysis of two superalloys used in casting of aircraft engine parts. The main aim of the research was to obtain the solidification parameters, especially Tsol and Tliq, knowledge of which is important for proper selection of casting and heat treatment parameters. Assessment of the metallurgical quality (presence of impurities) of the feed ingots is also a very important step in production of castings. It was found that some of the feed ingots delivered by the superalloy producers are contaminated by oxides located in shrinkage defects. The ATD analysis allows for quite precise interpretation of first stages of solidification at which solid phases with low values of latent heat of solidification are formed from the liquid. Using DSC analysis it is possible to measure precisely the heat values accompanying the phase changes during cooling and heating which, with knowledge of phase composition, permits to calculate the enthalpy of formation of specific phases like γ or γ′.
Go to article

Abstract

In order for the working status of the aluminum alloyed hydraulic valve body to be controlled in actual conditions, a new friction and wear design device was designed for the cast iron and aluminum alloyed valve bodies comparison under the same conditions. The results displayed that: (1) The oil leakage of the aluminum alloyed hydraulic valve body was higher than the corresponding oil leakage of the iron body during the initial running stage. Besides during a later running stage, the oil leakage of the aluminum alloyed body was lower than corresponding oil leakage of the iron body; (2) The actual oil leakage of different materials consisted of two parts: the foundation leakage that was the leakage of the valve without wear and wear leakage that was caused by the worn valve body; (3) The aluminum alloyed valve could rely on the dust filling furrow and melting mechanism that led the body surface to retain dynamic balance, resulting in the valve leakage preservation at a low level. The aluminum alloy modified valve body can meet the requirements of hydraulic leakage under pressure, possibly constituting this alloy suitable for hydraulic valve body manufacturing.
Go to article

Abstract

The results of investigations of the rheological properties of typical ceramic slurries used in the investment casting technology – the lost wax technology are presented in the paper. Flow curves in the wide range of shear velocity were made. Moreover, viscosity of ceramic slurries depending on shearing stresses was specified. Tests were performed under conditions of three different temperatures 25, 30 and 35oC, which are typical and important in the viewpoint of making ceramic slurries in the investment casting technology. In the light of the performed investigations can be said that the belonging in group of Newtonian or Non – Newtonian fluid is dependent on content of solid phase (addition of aluminum oxide) in the whole composition of liquid ceramic slurries.
Go to article

Abstract

Defects affect the properties and behavior of the casting during its service life. Since the defects can occur due to different reasons, they must be correctly identified and categorized, to enable applying the appropriate remedial measures. several different approaches for categorizing casting defects have been proposed in technical literature. They mainly rely on physical description, location, and formation of defects. There is a need for a systematic approach for classifying investment casting defects, considering appropriate attributes such as their size, location, identification stage, inspection method, consistency, appearance of defects. A systematic approach for categorization of investment casting defects considering multiple attributes: detection stage, size, shape, appearance, location, consistency and severity of occurrence. Information about the relevant attributes of major defects encountered in investment casting process has been collected from an industrial foundry. This has been implemented in a cloud-based system to make the system freely and widely accessible.
Go to article

Abstract

The results of researches of sorption processes of surface layers of components of sand moulds covered by protective coatings are presented in the hereby paper. Investigations comprised various types of sand grains of moulding sands with furan resin: silica sand, reclaimed sand and calcined in temperature of 700oC silica sand. Two kinds of alcoholic protective coatings were used – zirconium and zirconium – graphite. Tests were performed under condition of a constant temperature within the range 30 – 35oC and high relative air humidity 75 - 80%. To analyze the role of sand grains in sorption processes quantitavie moisture sorption with use of gravimetric method and ultrasonic method were used in measurements. The tendency to moisture sorption of surface layers of sand moulds according to the different kinds of sand grains was specified. The effectiveness of protective action of coatings from moisture sorption was analyzed as well. Knowledge of the role of sand grains from the viewpoint of capacity for moisture sorption is important due to the surface casting defects occurrence. In particular, that are defects of a gaseous origin caused by too high moisture content of moulds, especially in surface layers.
Go to article

Abstract

The article presents chosen aspects of foundry engineering of the settlement dwellers, including the archaeometric characteristics and metal science analysis of the artefacts, as well as an attempted reconstruction of the production organization. Discovered in Szczepidło (Greater Poland), the foundry workshop is unique in Central European Bronze Age. This workshop foundry operated roughly XIV-XII Century BC. Its production is evidenced by the presence of markers of the whole production cycle: semi-finished and finished products, production waste, fragments of crucibles and casting ladles with traces of usage, and tools. On this basis, the alloys and foundry technologies used have been described. The analysis of foundry technology of copper alloys in the settlement area was carried out by observing the surface and structure of the products, semi-finished artefacts and fragments of crucibles by applying optical microscopy (OM), confocal microscopy (CLSM) and Xray radiography (RT). The investigations of compositions were made by means of the energy dispersive X-ray fluorescence spectroscopy (ED-XRF) and scanning electron microscopy (SEM) coupled with an energy dispersive X-ray analysis system (EDS).
Go to article

Abstract

Measurements of the hardening process of the selected self-setting sands are presented in the hereby paper. Moulding sands were prepared on the matrix of „Szczakowa” sand of the Sibelco Company. Two resins: phenol-formaldehyde-furfuryl (FF/AF) and urea-formaldehydefurfuryl (MF/AF) were used for making moulding sands. – Methylbenzene-sulphonic acid was applied as a hardener for the moulding sand on FF/AF resin, while paratoluene-sulphonic acid for the moulding sand on MF/AF resin. Both hardeners were used in two concentrations: low – the so-called ‘slow’ hardener and high - ‘fast’ hardener. During investigations, the courses of the hardening process were determined, more accurately changes of the velocity of the ultrasound wave passage through the moulding sand cL = f(t) and changes of the moulding sand hardening degree versus time, Sx = f(t). In addition, the kinetics of the hardening process was determined. Measurements were performed on the research stand for ultrasound investigations.
Go to article

Abstract

High-tin bronzes are used for church bells and concert bells (carillons). Therefore, beside their decorative value, they should also offer other functional properties, including their permanence and good quality of sound. The latter is highly influenced by the structure of bell material, i.e. mostly by the presence of internal porosity which interferes with vibration of the bell waist and rim, and therefore should be eliminated. The presented investigations concerning the influence of tin content ranging from 20 to 24 wt% on mechanical properties of high-tin bronzes allowed to prove the increase in hardness of these alloys with simultaneous decrease in the tensile and the impact strengths (Rm and KV, respectively) for the increased tin content. Fractures of examined specimens, their porosity and microstructures were also assessed to explain the observed regularities. A reason of the change in the values of mechanical properties was revealed to be the change in the shape of α-phase crystals from dendritic to acicular one, and generation of grain structure related to the increased Sn content in the alloy.
Go to article

Abstract

An innovative method for determining the structural zones in the large static steel ingots has been described. It is based on the mathematical interpretation of some functions obtained due to simulation of temperature field and thermal gradient field for solidifying massive ingot. The method is associated with the extrema of an analyzed function and with its points of inflection. Particularly, the CET transformation is predicted as a time-consuming transition from the columnar- into equiaxed structure. The equations dealing with heat transfer balance for the continuous casting are presented and used for the simulation of temperature field in the solidifying virtual static brass ingot. The developed method for the prediction of structural zones formation is applied to determine these zones in the solidifying brass static ingot. Some differences / similarities between structure formation during solidification of the steel static ingot and virtual brass static ingot are studied. The developed method allows to predict the following structural zones: fine columnar grains zone, (FC), columnar grains zone, (C), equiaxed grains zone, (E). The FCCT-transformation and CET-transformation are forecast as sharp transitions of the analyzed structures. Similarities between steel static ingot morphology and that predicted for the virtual brass static ingot are described.
Go to article

Abstract

This study characterizes the bronze jewellery recovered from the Lusatian culture urn-field in Mała Kępa (Chełmno land, Poland). Among many common ornaments (e.g. necklaces, rings, pins) the ones giving evidence of a steppe-styled inspiration (nail earrings) were also identified. With the dendritic microstructures revealed, the nail earrings prove the implementing of a lost-wax casting method, whereas some of the castings were further subjected to metalworking. The elemental composition indicates the application of two main types of bronze alloys: Cu-Sn and Cu-Sn-Pb. It has been established that the Lusatian metalworkers were familiar with re-melting the scrap bronze and made themselves capable of roasting the sulphide-rich ores. The collection from Mała Kępa has been described in terms of its structure and composition. The investigations were made by means of the energy dispersive X-ray fluorescence spectroscopy (ED-XRF), scanning electron microscopy (SEM) coupled with an energy dispersive X - ray analysis system (EDS) and optical microscopy (OM). In order to fingerprint an alloy profile of the castings with a special emphasis on the nail earrings, the data-set (ED-XRF, EDS) was statistically evaluated using multidimensional analyses (FA, DA).
Go to article