The use of surface analysis to investigate brake elements shows how a pair in contact works and wears out during regular operation. The main purpose of this paper is to describe the asperities from initial state to a moment when further use of the drum and shoe is not possible. Between exchange of vital brake elements a truck with total mass exceeding 3.5 tons can cover as many as 300 000 kilometres. Use of brakes during the first 1000 kilometres after maintenance should be rather gentle with possibly intensive use of engine brake installed in the truck itself, because if this rule is not adhered to it may lead to a significant decrease of the braking force and on the surface of the pair in contact a layer will appear that is not possible to wear off and that will make it impossible to stop a truck using brakes. In that condition the shoe should be immediately replaced and the drum should be remachined (by turning) to a repair dimension. In the paper the condition and analysis of a surface after different course of exploitation was presented.
In the present work, the performance of multilayer coated carbide tool was investigated considering the effect of cutting parameters during turning of 34CrMo4 Low alloy steel. It has high strength and creep strength, and good impact tenacity at low temperature. It can work at –110°C to 500°C. And EN 10083-1 34CrMo4 owns high static strength, impact tenacity, fatigue resistance, and hardenability; without overheating tendencies. The objective functions were selected in relation to the parameters of the cutting process: surface roughness criteria. The correlations between the cutting parameters and performance measures, like surface roughness, were established by multiple linear regression models. Highly significant parameters were determined by performing an Analysis of variance (ANOVA). During the experiments flank wear, cutting force and surface roughness value were measured throughout the tool life. The results have been compared with dry and wet-cooled turning. Analysis of variance factors of design and their interactions were studied for their significance. Finally, a model using multiple regression analysis between cutting speed, fee rate and depth of cut with the tool life was established.
The wear behaviour of Cr3C2-25% NiCr laser alloyed nodular cast iron sample were analyzed using a pin-on-disc tribometer. The influence of sliding velocity, temperature and load on laser alloyed sample was focused and the microscopic images were used for metallurgical examination of the worn-out sites. Box-Behnken method was utilised to generate the mathematical model for the condition parameters. The Response Surface Methodology (RSM) based models are varied to analyse the process parameters interaction effects. Analysis of variance was used to analyse the developed model and the results showed that the laser alloyed sample leads to a minimum wear rate (0.6079×10–3 to 1.8570×10–3 mm3/m) and coefficient of friction (CoF) (0.43 to 0.53). From the test results, it was observed that the experimental results correlated well with the predicted results of the developed mathematical model.
The present investigation has been made to assess the influence of B4C reinforced with Ti-6Al-4V matrix prepared by powder metallurgy route. High energy ball milling was used to prepare the composites. Cylindrical preforms were prepared using suitable die set assembly. The green preforms were sintered in the muffle furnace at 900°C for 1 h. Further the preforms were cooled inside the furnace till the room temperature has attained. SEM with EDS mapping analysis was used to evaluate the morphology and elemental confirmation of the prepared composite. The density and hardness of the samples are determined using Archimedes principle and Rockwell hardness testing machine. The wear resistance of the samples was determined by employing a pin on disc apparatus. The hardness of the composites (Ti-6Al-4V /10B4C) was increased while comparing to the base material (Ti-6Al-4V) which is attributed to the presence of hard ceramic phase. Response Surface Methodology (RSM) five level central composite design approach was accustomed and it minimised the amount of experimental conditions and developed mathematical models among the key process parameters namely wt. % of B4C, applied load and sliding distances to forecast the abrasive response of Specific Wear Rate (SWR) and Coefficient of Friction (CoF). Analysis of variance was used to check the validity of the developed model. The optimum parameters of specific wear rate and coefficient of friction were identified.
This paper discusses changes in the microstructure and abrasive wear resistance of G17CrMo5-5 cast steel modified with rare earth metals (REM). The changes were assessed using scanning microscopy. The wear response was determined in the Miller test to ASTM G75. Abrasion tests were supplemented with the surface profile measurements of non-modified and modified cast steel using a Talysurf CCI optical profilometer. It was demonstrated that the modification substantially affected the microstructure of the alloy, leading to grain size reduction and changed morphology of non-metallic inclusions. The observed changes in the microstructure resulted in a three times higher impact strength (from 33 to 99 kJ/cm2 ) and more than two times higher resistance to cracking (from 116 to 250 MPa). The following surface parameters were computed: Sa: Arithmetic mean deviation of the surface, Sq: Root-mean-square deviation of the surface, Sp: Maximum height of the peak Sv: Maximum depth of the valley, Sz: Ten Point Average, Ssk: Asymmetry of the surface, Sku: Kurtosis of the surface. The findings also indicated that the addition of rare earth metals had a positive effect on the abrasion behaviour of G17CrMo5-5 cast steel.
The dry sliding wear behavior of heat-treated super duplex stainless steel AISI 2507 was examined by taking pin-on-disc type of wear-test rig. Independent parameters, namely applied load, sliding distance, and sliding speed, influence mainly the wear rate of super duplex stainless steel. The said material was heat treated to a temperature of 850°C for 1 hour followed by water quenching. The heat treatment was carried out to precipitate the secondary sigma phase formation. Experiments were conducted to study the influence of independent parameters set at three factor levels using the L27 orthogonal array of the Taguchi experimental design on the wear rate. Statistical significance of both individual and combined factor effects was determined for specific wear rate. Surface plots were drawn to explain the behavior of independent variables on the measured wear rate. Statistically, the models were validated using the analysis of variance test. Multiple non-linear regression equations were derived for wear rate expressed as non-linear functions of independent variables. Further, the prediction accuracy of the developed regression equation was tested with the actual experiments. The independent parameters responsible for the desired minimum wear rate were determined by using the desirability function approach. The worn-out surface characteristics obtained for the minimum wear rate was examined using the scanning electron microscope. The desired smooth surface was obtained for the determined optimal condition by desirability function approach.