This paper shows results of researches of a structure and mechanical properties of metal sheets of IF steels subjected torecrystallization annealing. The annealing was held in the scope of the temperature of 600-900°C over 25 min time. The impact of heat treatment on changes of properties and structure of the researches steel has been analysed. During annealing typical processes of rebuilding of the structure deformed as a result of cold deformation in the form of forming new recrystallized grains and their growth were observed. As the temperature of annealing increases the hardness of the material gradually decreases.
Go to article

Abstract

The effect of CaSiAl modification (43-49% Ca, 43-48% Si, 2% Al) on the non-metallic inclusions and mechanical properties of cast lowcarbon steel is discussed. Tests were carried out on the cast steel with 0.2% C and micro-additives of V and Nb, used mainly for heavy steel castings (e.g. slag ladles). The modifier in an amount of 1.5 and 3 kg / Mg was introduced to the liquid steel before tapping the metal into a ladle. Test ingots of Y type and a weight of 10 kg were cast and then subjected to a normalizing heat treatment. Using light microscopy and scanning electron microscopy, qualitative and quantitative evaluation of the non-metallic inclusions present in as-cast samples was carried out. Additionally, tests of mechanical strength and impact strength were performed on cast steel with and without the different content of modifier. It was found that increasing the modifier addition affected impact strength but had no significant effect on tensile strength and yield strength. The material with high impact strength had the smallest area fraction of non-metallic inclusions in the microstructure (0.20%). The introduction of modifiers changed the morphology of non-metallic inclusions from dendritic to regular and nodular shapes.
Go to article

This page uses 'cookies'. Learn more