Abstract

The article presents the results of research on the finishing of M63 Z4 brass by vibratory machining. Brass alloy was used for the research due to the common use of ammunition elements, cartridge case and good cold forming properties on the construction. Until now, the authors have not met with the results of research to determine the impact of abrasive pastes in container processing. It was found that the additive for container abrasive treatment of abrasive paste causes larger mass losses and faster surface smoothing effects. The treatment was carried out in two stages: in the first stage, the workpieces were deburred and then polished. Considerations were given to the impact of mass of workpieces, machining time and its type on mass loss and changes in the geometric structure of the surface. The surface roughness of machining samples was measured with the Talysurf CCI Lite optical profiler. The suggestions for future research may be to carry out tests using abrasive pastes with a larger granulation of abrasive grains, and to carry out tests for longer processing times and to determine the time after which the parameters of SGP change is unnoticeable.
Go to article

Abstract

Paper present a thermal analysis of laser heating and remelting of EN AC-48000 (EN AC-AlSi12CuNiMg) cast alloy used mainly for casting pistons of internal combustion engines. Laser optics were arranged such that the impingement spot size on the material was a circular with beam radius rb changes from 7 to 1500 m. The laser surface remelting was performed under argon flow. The resulting temperature distribution, cooling rate distribution, temperature gradients and the depth of remelting are related to the laser power density and scanning velocity. The formation of microstructure during solidification after laser surface remelting of tested alloy was explained. Laser treatment of alloy tests were perform by changing the three parameters: the power of the laser beam, radius and crystallization rate. The laser surface remelting needs the selection such selection of the parameters, which leads to a significant disintegration of the structure. This method is able to increase surface hardness, for example in layered castings used for pistons in automotive engines.
Go to article

Abstract

Residual stress has a great influence on the metal, but it is difficult to measure at small area using a general method. Residual stress calculations using the Vickers indentation can solve this problem. In this paper, a numerical simulation has been made for the residual stress measurement method of metal material deformed by high-speed impact. Then, the stress-strain curve at the high-speed deformation was confirmed through actual experiments, and the residual stresses generated thereafter were calculated by the Vickers indenter method. A Vickers indentation analysis under the same conditions was performed at the position where a residual stress of about 169.39 MPa was generated. Experiments were carried out and high speed impact was applied to the specimen to generate residual stress. The obtained results indicate that it is possible to identify residual stresses in various metals with various shapes through Vickers indentation measurements, and to use them for process and quality control.
Go to article

Abstract

Aluminum alloys are widely used today in plastic injection molds in the automotive and aerospace industries due to their high strength and weight ratio, good corrosion and fatigue resistance as well as high feed rates. The 5754 aluminum alloy has high corrosion resistance and a structure suitable for cold forming. In this study, an AA 5754-H111 tempered aluminum alloy with the dimensions of 80×80×30 mm was used, and some of the materials were cryogenically heat treated. For the milling operations, ϕ12 mm diameter 76 mm height uncoated as well as TiCN and TiAlN coated end mills were used. Different levels of cutting depth (1.25, 2.0, 2.5 mm), cutting speed (50, 80, 100 m/ min), feed rate (265, 425, 530 m/ min) and machining pattern (concentric, back and forth and inward helical) were used. The number of experiments was reduced from 486 to 54 using the Taguchi L54 orthogonal array. The values obtained at the end of the experiments were evaluated using the signal-to-noise ratio, ANOVA, three-dimensional graphs and the regression method. Based on the result of the verification experiments, the processing accuracy for surface roughness was improved from 3.20 μm to 0.90 μm, with performance increase of 71.88%.
Go to article

Abstract

The modified surface layers of Mg enriched with Al and Si were fabricated by thermochemical treatment. The substrate material in contact with an Al + 20 wt.% Si powder mixture was heated to 445ºC for 40 or 60 min. The microstructure of the layers was examined by OM and SEM. The chemical composition of the layer and the distribution of elements were determined by energy dispersive X-ray spectroscopy (EDS). The experimental results show that the thickness of the layer is dependent on the heating time. A much thicker layer (1 mm) was obtained when the heating time was 60 min than when it was 40 min (600 μm). Both layers had a non-homogeneous structure. In the area closest to the Mg substrate, a thin zone of a solid solution of Al in Mg was detected. It was followed by a eutectic with Mg17Al12and a solid solution of Al in Mg. The next zone was a eutectic with agglomerates of Mg2Si phase particles; this three-phase structure was the thickest. Finally, the area closest to the surface was characterized by dendrites of the Mg17Al12phase. The microhardness of the modified layer increased to 121-236 HV as compared with 33-35 HV reported for the Mg substrate.
Go to article

Abstract

Al- and Al/Zn-enriched layers containing intermetallic phases were deposited on the Mg substrate by heating the Mg specimens in contact with the powdered materials in a vacuum furnace. The Al-enriched surface layers were produced using Al powder, whereas the Al/Znenriched layers were obtained from an 80 wt.% Al + 20 wt.% Zn powder mixture. The microstructure and composition of the layers were analyzed by optical microscopy, scanning electron microscopy and X-ray diffraction. The results showed that the Al-enriched layer comprised an Mg17Al12 intermetallic phase and a solid solution of Al in Mg. The layer obtained from the Al+Zn powder mixture was composed of Mg-Al-Zn intermetalic phases and a solid solution of Al and Zn in Mg. Adding 20% of Zn into the Al powder resulted in the formation of a considerably thicker layer. Moreover, the hardness of the surface layers was much higher than that of the Mg substrate.
Go to article

Abstract

This paper deals with the evaluation of the corrosion resistance of the Al-Si alloys alloyed with the different amount of antimony. Specifically it goes about the alloy AlSi7Mg0,3 which is antimony alloyed in the concentrations 0; 0,001; 0,005; 0,01 a 0,05 wt. % of antimony. The introduction of the paper is dedicated to the theory of the aluminium alloys corrosion resistance, testing and evaluation of the corrosion resistance. The influence of the antimony to the Al-Si alloys properties is described further in the introduction. The experimental part describes the experimental samples which were prepared for the experiment and further they were exposed to the loading in the atmospheric conditions for a period of the 3 months. The experimental samples were evaluated macroscopically and microscopically. The results of the experiment were documented and the conclusions in terms of the antimony impact to the corrosion resistance of the Al-Si alloy were concluded. There was compared the corrosion resistance of the Al-Si alloy antimony alloyed (with the different antimony content) with the results of the Al-Si alloy without the alloying after the corrosion load in the atmospheric conditions in the experiment.
Go to article