The paper presents the results and provides an analyse of the geometric structure of Fe-Al protective coatings, gas-treated under specified GDS conditions. The analysis of the surface topography was conducted on the basis of the results obtained from the SEM data. Topographic images were converted to three-dimensional maps, scaling the registered amplitude coordinates of specific gray levels to the relative range of 0÷1. This allowed us to assess the degree of surface development by determining the fractal dimension. At the same time, the generated three-dimensional spectra of the autocorrelation function enabled the researchers to determine the autocorrelation length (Sal) and the degree of anisotropy (Str) of the surfaces, in accordance with ISO 25178. Furthermore, the reconstructed three-dimensional images of the topography allowed us to evaluate the functional properties o the studied surfaces based on the Abbott-Firestone curve (A-F), also known as the bearing area curve. The ordinate describing the height of the profile was replaced by the percentage of surface amplitude in this method, so in effect the shares of the height of the three-dimensional topographic map profiles of various load-bearing properties were determined. In this way, both the relative height of peaks, core and recesses as well as their percentages were subsequently established.
The results of structure observations of Ni base superalloy subjected to long-term influence of high pressure hydrogen atmosphere at 750K and 850K are presented. The structure investigation were carried out using conventional light-, scanning- (SEM) and transmission electron microscopy (TEM). The results presented here are supplementary to the mechanical studies given in part I of this investigations. The results of study concerning mechanical properties degradation and structure observations show that the differences in mechanical properties of alloy subjected different temperature are caused by more advanced processes of structure degradation during long-term aging at 850K, compare to that at 750K. Higher service temperature leads to formation of large precipitates of δ phase. The nucleation and growth of needle- and/or plate-like, relative large delta precipitates proceed probably at expense strengthening γ" phases. Moreover, it can't be excluded that the least stable γ" phase is replaced with more stable γ' precipitates. TEM observations have disclosed differences in dislocation structure of alloy aged at 750K and 850K. The dislocation observed in alloy subjected to 750K are were seldom observed only, while in that serviced at high stress and 850K dislocation array and dislocation cell structure was typical.
In the work five ceramic compounds based on the (K0.44Na0.52Li0.04)NbO3 (KNLN) material modified with oxides: Cr2O3, ZnO, Sb2O3 or Fe2O3 (in an amount of 0.5 mol.%) were obtained. The KNLN-type composition powder was prepared by solid phase synthesis from a mixture of simple oxides and carbonates, while compacted of the ceramic samples was conducted by free sintering methods. In the work the effect of the used admixture on the electrophysical properties of the KNLN ceramics was presented. The XRD, EDS tests, the SEM measurements of the morphology ceramic samples, dielectric properties and DC electric conductivity were conducted. The research showed that the used admixtures introduced into the base of KNLN-type composition improve the microstructure of the ceramic samples and improve their sinterability. In the case of the dielectric measurements, it was observed a decrease in the maximum dielectric permittivity at the TC for dopred KNLN-type samples. The addition of an admixture of chromium, zinc, antimony or iron in an amount of 0.5 mol.% to the base composition (K0.44Na0.52Li0.04)NbO3 practically does not change the phase transition temperature. The diminution in the density value of doped KNLN ceramics was attributed to the alkali elements volatilization.
Detailed studies on the effects of pulsed laser interference heating on surface characteristics and subsurface microstructure of amorphous Fe80Si11B9 alloy are reported. Laser interference heating, with relatively low pulsed laser energy (90 and 120 mJ), but with a variable number (from 50-500) of consecutive laser pulses permitted to get energy accumulation in heated areas. Such treatment allowed to form two- Dimensional micro-islands of laser-affected material periodically distributed in amorphous matrix. The crystallization process of amorphous FeSiB ribbons was studied by means of scanning and transmission electron microscopy. Detailed microstructural examination showed that the use of laser beam, resulted in development of nanostructure in the heated areas of the amorphous ribbon. The generation of nanocrystalline seed islands created by pulsed laser interference was observed. This key result may evidently give new knowledge concerning the differences in microstructure formed during the conventional and lased induced crystallization the amorphous alloys. Further experiments are needed to clarify the effect of pulsed laser interference crystallization on magnetic properties of these alloys.
Investigations were carried out to ensure the granulated blast furnace (GBF) slag as an alternative mould material in foundry industry by assessing the cast products structure property correlations. Sodium silicate-CO2 process was adopted for preparing the moulds. Three types of moulds were made with slag, silica sand individually and combination of these two with 10% sodium silicate and 20 seconds CO2 gassing time. A356 alloy castings were performed on these newly developed slag moulds. The cast products were investigated for its metallography and mechanical properties. Results reveal that cast products with good surface finish and without any defects were produced. Faster heat transfers in slag moulds enabled the cast products with fine and refined grain structured; and also, lower Secondary Dendrite Arm Spacing (SDAS) values were observed than sand mould. Slag mould casting shows improved mechanical properties like hardness, compression, tensile and impact strength compared to sand mould castings. Two types of tensile fracture modes, namely cleavage pattern with flat surfaces representing Al−Si eutectic zone and the areas of broken Fe-rich intermetallic compounds which appear as flower-like morphology was observed in sand mould castings. In contrast, GBF slag mould castings exhibit majority in dimple fracture morphology with traces of cleavage fracture. Charpy impact fractured surfaces of sand mould castings shows both transgranular and intergranular fracture modes. Only intergranular fracture mode was noticed in both GBF slag and mixed mould castings.
The paper presents the effect of pre-heat treatment on the mechanical properties of ductile cast iron with elevated content of Cu and Mo elements. Austempered Ductile Iron is a material with non-standard properties, combining high tensile strength and abrasion resistance with very good plasticity. In addition, it is prone to strain hardening and have good machining abilities. The study was conducted for five designed heat treatment cycles. The variables were the time and temperature of the pre-heat treatment, followed by one of two standard heat treatments for ADI cast iron. The aim of the authors was fragmentation of the grains of perlite during the initial heat treatment. It is presumed, that subsequent heat treatment will cause further refinement of the microstructure than would be the case without initial heat treatment. Diffusion is much faster than in case of ferritic matrix of cast iron. The results will be used to evaluate material for the production of parts of equipment that must operate under extreme load conditions.