Flake graphite cast iron was hot-dip coated with pure aluminium or aluminium alloys (AlSi11 and AlTi5). The study aimed at determining the influence of bath composition on the thickness, microstructure and phase composition of the coatings. The analysis was conducted by means of an optical microscope and a scanning electron microscope with an EDS spectrometer. It was found that the overall thickness of a coating was greatly dependent on the chemical composition of a bath. The coatings consisted of an outer layer and an inner intermetallic layer, the latter with two zones and dispersed graphite. In all the cases considered, the zone in the inner intermetallic layer adjacent to the cast iron substrate contained the Al5Fe2 phase with small amount of silicon; the interface between this phase and the cast iron substrate differed substantially, depending on the bath composition. In the coatings produced by hot-dipping in pure aluminium the zone adjacent to the outer layer had a composition similar to that produced from an AlTi5 bath, the Al3Fe phase was identified in this zone. The Al3Fe also contained silicon but its amount was lower than that in the Al5Fe2. In the coatings produced by hot-dipping in AlSi11, the zone adjacent to the outer layer contained the Al3FeSi phase. The analysis results showed that when AlSi11 alloy was applied, the growth mode of the inner layer changed from inwards to outwards. The interface between the Al5Fe2 phase and the cast iron substrate was flat and the zone of this phase was very thin. Locally, there were deep penetrations of the Al5FeSi phase into the outer layer, and the interface between this phase and the outer layer was irregular. Immersion in an AlTi5 bath caused that the inner intermetallic layer was thicker than when pure aluminium or AlSi11 alloy baths were used; also, some porosity was observed in this layer; and finally, the interface between the inner layer and the cast iron substrate was the most irregular.
Go to article

Abstract

In this paper are presented results of study fusion characteristics of the biomass ashes from the hydrolyzed lignin and the ashes from the coke breeze. The hydrolyzed lignin ashes were compared with the coke breeze ashes i.e. with a fossil fuel. These ashes were prepared in muffle furnace at the temperature of 550°C (hydrolyzed lignin) and 850°C (coke breeze). Biomass (the hydrolyzed lignin) represents the new fuels for sintering process and an attractive way to decrease CO2 emissions from the energy production. The characterization methods were the following: standard fuel characterization analyses, chemical and mineralogical composition of the ashes and phase analyses of the ashes of biomass and the coke breeze. These ashes were prepared by the same method. Characterisation of the ashes samples was conducted by means of X-ray fluorescence (XRF), X-ray diffraction (XRD) and scanning electron microscopy (SEM). Quantitative analysis of the crystalline and amorphous phases in each of the ash samples were carried out using the Rietveld method. The dominant phase of the ash from the coke breeze was mullite (Al6Si2O13). SiO2 is the dominant phase of the ash from the hydrolyzed lignin.
Go to article

Abstract

This paper deals with influence on segregation of iron based phases on the secondary alloy AlSi7Mg0.3 microstructure by nickel. Iron is the most common and harmful impurity in aluminum casting alloys and has long been associated with an increase of casting defects. In generally, iron is associated with the formation of Fe-rich intermetallic phases. It is impossible to remove iron from melt by standard operations. Some elements eliminates iron by changing iron intermetallic phase morphology, decreasing its extent and by improving alloy properties. Realization of experiments and results of analysis show new view on solubility of iron based phases during melt preparation with higher iron content and influence of nickel as iron corrector of iron based phases.
Go to article

Abstract

This paper deals with influence on segregation of iron based phases on the secondary alloy AlSi7Mg0.3 microstructure by chrome. Iron is the most common and harmful impurity in aluminum casting alloys and has long been associated with an increase of casting defects. In generally, iron is associated with the formation of Fe-rich phases. It is impossible to remove iron from melt by standard operations, but it is possible to eliminate its negative influence by addition some other elements that affect the segregation of intermetallics in less harmful type. Realization of experiments and results of analysis show new view on solubility of iron based phases during melt preparation with higher iron content and influence of chrome as iron corrector of iron based phases. By experimental work were used three different amounts of AlCr20 master alloy a three different temperature of chill mold. Our experimental work confirmed that chrome can be used as an iron corrector in Al-Si alloy, due to the change of intermetallic phases and shortening their length.
Go to article

Abstract

This paper deals with influence of chrome addition and heat treatment on segregation of iron based phases in the secondary alloy AlSi7Mg0.3 microstructure by chrome and heat treatment. Iron is the most common and harmful impurity in aluminum casting alloys and has long been associated with an increase of casting defects. In generally, iron is associated with the formation of Fe-rich intermetallic phases. It is impossible to remove iron from melt by standard operations, but it is possible to eliminate its negative influence by addition some other elements that affect the segregation of intermetallics in less harmful type or by heat treatment. Realization of experiments and results of analysis show new view on solubility of iron based phases during melt preparation with higher iron content and influence of chrome as iron corrector of iron based phases.
Go to article

Abstract

In Al-Si alloy the iron is the most common impurity and with presence of other elements in alloy creates the intermetallic compounds, which decreases mechanical properties and increases of porosity. The cause of the negative effect of intermetallic particles on the mechanical properties is that it is more easily break off the tension load as the aluminium matrix or small particles of silicon. By adding suitable alloying elements, also known as iron correctors, is possible to reduce this harmful effect. In the article is evaluated influence of manganese on microstructure with performed EDX analysis selected intermetallic phases and tensile test and measurement of length of Al5FeSi phase. For realization experiments was used AlSi7Mg0.3 alloy with increased iron content. Manganese was added in the amount 0.3 wt. %, 0.6 wt. %, 0.8 wt.% and 1,2 wt. %. From performed measurements it has been concluded, that increased amount of manganese, i.e. Mn/Fe ratio, does not have significant influence on mechanical properties AlSi7Mg0.3 alloy in the melted state.
Go to article