One of the methods to prevent unsuitable lubrication of moving components of devices and machinery is using bi-metal and three-metal bearings. Centrifugal casting process is one of the manufacturing methods that is used for such bearings. In this study, the purpose is microstructure evaluation of the bonding location and length determination of diffusion bond in structural steel-bronze. A mold made of structural steel with inner diameter of 240mm, length of 300mm and thickness of 10mm was coated by a 6mm film of bronze under centrifugal casting process. At first, a bronze ingot with dimension of 5mm×10mm×20mm is located inside of the hollow cylindrical mold and then the two ends of it will be sealed. During mold rotation with the rate of 800 rpm, two high power flames are used for heating the mold under Ar gas atmosphere to melt the bronze ingot at 1000˚C. After 15minutes, the system is cooled rapidly. Results showed that the diffusion bonding of bronze in structural steel to depth of 1.2µm from the bonding line was obtained. In this bonding, copper element was diffused to 50% of its initial concentration.
The paper presents the results of investigation into the technological possibility of making light-section castings of GX2CrNiMoN25-6-3 cast steel. For making castings with a wall thickness in the thinnest place as small as below 1 mm, the centrifugal casting technology was employed. The technology under consideration enables items with high surface quality to be obtained, while providing a reduced consumption of the charge materials and, as a result, a reduction in the costs of unit casting production.
The results of castability and structures researches of two nickel base alloys - Ceranium CN and Magnum AN applied on casting of the crowns and dental bridges are presented. Studies were carried out on the alloys cast under the centrifugal force to the moulds made by the lost wax method using production line of ROKO. Having regard to a specific technology of casting and possibility of ROKO production line, to the estimation of alloys castability a spiral test was adjusted with a 0,8 mm and a 2,5 mm diameter of test casting. Measuriements executed on a 20 test castings allowed to establish, that castability of Magnum AN alloy was 65 % greater than castability of Ceranium NC alloy. The results of thermodynamics calculations of the equilibrium and nonequilibrium crystallization (Scheil model) of the investigated alloys are presented too. The characteristic temperatures of phase transformation and forecast phase composition of alloys for both kind of crystallization were calculated. It is established after structural supervisions, that the investigated alloys crystallize in dendryte form and in centrifugal casting conditions have cooling rate sensivity and inclination to texture structure forming in outmost layer of casting. Phase composition of alloys corresponds to the results of thermodynamics calculations of the nonequilibrium crystallization conditions.
Silicon bronzes are characterised by good mechanical properties and by high corrosion and mechanical wear resistance. The process of sleeve casting by means of the centrifugal casting with the horizontal axis of the mould rotation was analysed. The assessment of the influence of modification and centrifugal casting parameters on the microstructure and mechanical properties of alloys was carried out in the hereby work. Zirconium was applied as a modifier. Speed of rotation of the mould was the variable parameter of the centrifugal casting. The investigation results were summarised on the basis of the microstructure analysis and mechanical properties determination: UTS, proof stress, A10 and BHN. The experiment aimed at finding the information in which way the modification together with changing the pouring parameters influence the mechanical properties of the CuSi3Zn3FeMn alloy.