An analysis has been carried out of the influence of annealing time at the preheating temperature of 650 °C on the change in hardness and alloy structure of lamellar graphite cast iron in the working as well as in the laboratory conditions. This preheat temperature is common during reclaiming welding of castings with complex shapes. The changes in unalloyed cast iron EN-GJL 200 to EN-GJL 300 according to ISO 1690 standard and cast iron with low amount of elements such as Sn, Cu, Cr, and Mo and their combinations were assessed. It was found that the cast iron of higher strength grades has better hardness and structural stability. Cast iron alloyed with chromium or its combinations has the highest stability. In unalloyed cast iron, a partial degradation of pearlite occurs; in alloyed cast iron the structural changes are not conclusive.
The paper presents the initial results of investigation concerning the abrasion resistance of cast iron with nodular, vermicular, or flake graphite. The nodular and vermicular cast iron specimens were cut out of test coupons of the IIb type with the wall thickness equal to 25 mm, while the specimens made of grey cast iron containing flake graphite were cut out either of special casts with 20 mm thick walls or of the original brake disk. The abrasion tests were carried out by means of the T-01M tribological unit working in the pin-on-disk configuration. The counterface specimens (i.e. the disks) were made of the JT6500 brand name friction material. Each specimen was abraded over a distance of 4000 m. The mass losses, both of the specimens and of the counterface disks, were determined by weighting. It was found that the least wear among the examined materials was exhibited by the nodular cast iron. In turn, the smallest abrasion resistance was found in vermicular cast iron and in cast iron containing flake graphite coming from the brake disk. However, while the three types of specimens (those taken from the nodular cast iron and from grey cast iron coming either from the special casts or from the brake disk) have almost purely pearlitic matrix (P95/Fe05), the vermicular cast iron matrix was composed of pearlite and ferrite occurring in the amounts of about 50% each (P50/Fe50). Additionally, it was found that the highest temperature at the cast iron/counterface disk contact point was reached during the tests held for the nodular cast iron, while the lowest one occurred for the case of specially cast grey iron.
In this paper results of microstructural observations for series of CuZn39Pb2 alloys produced from qualified scraps are presented. The individual alloy melts were differentiated in terms of thermal parameters of continuous casting as well as refining methods and modifications. Structural observations performed by SEM and TEM revealed formation of different types of intermetallic phases including “hard particles”. EDS results show that “hard particles” are enrich in silicon, phosphorus, iron, chromium and nickel elements. Additionally, formation of Al-Fe-Si and Al-Cr in alloy melts was observed as well. It was found that quantity and morphology of intermetallic phases strongly depends upon the chemical composition of raw materials, process parameters, modifiers and refining procedure applied during casting. It was observed that refining process results in very effective refinement of intermetallic phases, whereas modifiers, particularly carbon-based, results in formation of large particles in the microstructure.
This paper presents results of a research on the possibilities of applying 3D printed casting models for small production series as alternative to traditional tooling production on automated DisaMatch mould production lines. The main task was to verify and compare the dimensions of the 3D printed models before and after moulding process. The paper discusses main advantages and disadvantages of the 3D printing methods used like FDM (Fused Deposition Modeling)/FFF (Fused Filament Fabrication), SLA (stereolitography) and DPP (Daylight Polymer Printing). Measurement of casting model outside dimension change resulting from moulding sand friction on their surface was made with the use of GOM INSPECT software on the basis of 3D scans made with ATOS TripleScan optical scanner. Hardness of 3D printed models made of ABS, Z-ULTRAT, three different photopolymer resins (from FormLab and Liquid Crystal companies) was verified. The result of the research printed models usability for the foundry industry was presented.
The paper consists the problem of developing a scientific toolkit allowing to predict the thermal state of the ingot during its formation in all elements of the casting and rolling complex, between the crystallizer of the continuous casting machine and exit from the furnace. As the toolkit for the decision making task the predictive mathematical model of the ingot temperature field is proposed. Displacement between the various elements of the CRC is accounted for by changing the boundary conditions. Mass-average enthalpy is proposed as a characteristic of ingot cross-section temperature state. The next methods of solving a number of important problems with the use of medium mass enthalpy are developed: determination of the necessary heat capacity of ingots after the continuous casting machine for direct rolling without heating; determination of the rational time of alignment of the temperature field of ingots having sufficient heat capacity for rolling after casting; determination of the total amount of heat (heat capacity) required to supply the metal for heating ingots that have insufficient amount of internal heat.
Results of a research on influence of chromium, molybdenum and aluminium on structure and selected mechanical properties of Ni-Mn-Cu cast iron in the as-cast and heat-treated conditions are presented. All raw castings showed austenitic matrix with relatively low hardness, making the material machinable. Additions of chromium and molybdenum resulted in higher inclination to hard spots. However, a small addition of aluminium slightly limited this tendency. Heat treatment consisting in soaking the castings at 500 °C for 4 h resulted in partial transformation of austenite to acicular, carbon-supersaturated ferrite, similar to the bainitic ferrite. A degree of this transformation depended not only on the nickel equivalent value (its lower value resulted in higher transformation degree), but also on concentrations of Cr and Mo (transformation degree increased with increasing total concentration of both elements). The castings with the highest hard spots degree showed the highest hardness, while hardness increase, caused by heat treatment, was the largest in the castings with the highest austenite transformation degree. Addition of Cr and Mo resulted in lower thermodynamic stability of austenite, so it appeared a favourable solution. For this reason, the castings containing the highest total amount of Cr and Mo with an addition of 0.4% Al (to reduce hard spots tendency) showed the highest tensile strength.
Ablation casting is a technological process in which the increased cooling rate causes microstructure refinement, resulting in improved mechanical properties of the final product. This technology is particularly suitable for the manufacture of castings with intricate shapes and thin walls. Currently, the ablation casting process is not used in the Polish industry. This article presents the results of strength tests carried out on moulding sands based on hydrated sodium silicate hardened in the Floster S technology, intended for ablation casting of the AlSi7Mg (AK7) aluminium alloy. When testing the bending and tensile strengths of sands, parameters such as binder and hardener content were taken into account. The sand mixtures were tested after 24h hardening at room temperature. The next stage of the study describes the course of the ablation casting process, starting with the manufacture of foundry mould from the selected moulding mixture and ending in tests carried out on the ready casting to check the surface quality, structure and mechanical properties. The results were compared with the parallel results obtained on a casting gravity poured into the sand mould and solidifying in a traditional way at ambient temperature.
Definition of a composite  describes an ideal composite material with perfect structure. In real composite materials, structure is usually imperfect – composites contain various types of defects [2, 3–5], especially as the casted composites are of concern. The reason for this is a specific structure of castings, related to course of the manufacturing process. In case of metal matrix composite castings, especially regarding these manufactured by saturation, there is no classification of these defects [2, 4]. Classification of defects in castings of classic materials (cast iron, cast steel, non-ferrous alloys) is insufficient and requires completion of specific defects of mentioned materials. This problem (noted during manufacturing metal matrix composite castings with saturated reinforcement in Institute of Basic Technical Sciences of Maritime University Szczecin) has become a reason of starting work aimed at creating such classification. As a result, this paper was prepared. It can contribute to improvement of quality of studied materials and, as a consequence, improve the environment protection level.
Early Buddhism was a predominantly spiritual movement which should ideally culminate in Enlightenment. Yet, it was embedded in the specific social environment of ancient India which included a hereditary caste system. Using the Buddhist Pāli texts and non-Buddhist literature from up until the last centuries BCE the article examines the four main hereditary categories (vaṇṇa, jāti, gotta, and kula) and how Early Buddhism related to them. We conclude that the Buddha and Early Buddhism did not oppose but rather confirmed the hereditary systems in society as well as its designations within the monastic community. The Buddha hereby followed the customs of earlier ascetic movements and imposed no specific rules on the monastics to eradicate their former social identity.
Investment casting combined with the additive manufacturing technology enables production of the thin-walled elements, that are geometrically complex, precise and can be easy commercialized. This paper presents design of aluminium alloy honeycombs, which are characterized with light structure, internal parallel oriented channels and suitable stiffness. Based on 3D printed pattern the mould was prepared from standard ceramic material subjected subsequently to appropriate heat treatment. Into created mould cavity with intricate and susceptible structure molten AC 44200 aluminium alloy was poured under low pressure. Properly designed gating system and selected process parameters enabled to limit the shrinkage voids, porosities and misruns. Compression examination performed in two directions showed different mechanisms of cell deformation. Characteristic plateau region of stress-strain curves allowed to determine absorbed energy per unit volume, which was 485 or 402 J/mm3 depending on load direction. Elaborated technology will be applied for the production of honeycomb based elements designated for energy absorption capability.
Final quality of casts produced in a die casting process represents a correlation of setting of technological parameters of die casting cycle, properties of alloy, construction of a die and structure of gating and of bleeding systems. Suitable structure of a gating system with an appertaining bleeding system of the die can significantly influence mechanical and structural properties of a cast. The submitted paper focuses on influence of position of outfall of an gate into the cast on its selected quality properties. Layout of the test casts in the die was designed to provide filling of a shaping cavity by the melt with diverse character of flowing. Setting of input technological parameters during experiment remained on a constant level. The only variable was the position of the gate. Homogeneity represented by porosity f and ultimate strength Rm were selected to be the assessed representative quality properties of the cast. The tests of the influence upon monitored parameters were realized in two stages. The test gating system was primarily subjected to numerical tests with the utilization of a simulation program NovaFlow&Solid. Consequently, the results were verified by the experimental tests carried out with the physical casts produced during operation. It was proved that diverse placement of the gate in relation to the cast influences the mode of the melt flowing through the shaping cavity which is reflected in the porosity of the casts. The experimental test proved correlation of porosity f of the cast with its ultimate strength Rm. At the end of the paper, the interaction dependencies between the gate position, the mode of filling the die cavity, porosity f and ultimate strength Rm.
The mathematical model and numerical simulations of the solidification of a cylindrical shaped casting, which take into account the process of filling the mould cavity by liquid metal and feeding the casting through the riser during its solidification, are presented in the paper. Mutual dependence of thermal and flow phenomena were taken into account because have an essential influence on solidification process. The effect of the riser shape on the effectiveness of feeding of the solidifying casting was determined. In order to obtain the casting without shrinkage defects, an appropriate selection of riser shape was made, which is important for foundry practice. Numerical calculations of the solidification process of system consisting of the casting and the conical or cylindrical riser were carried out. The velocity fields have been obtained from the solution of momentum equations and continuity equation, while temperature fields from solving the equation of heat conductivity containing the convection term. Changes in thermo-physical parameters as a function of temperature were considered. The finite element method (FEM) was used to solve the problem.
Heavy steel castings deoxidized with aluminium are sometimes brittle intercrystalline failed during their service along primary grain boundaries what is initiated by aluminium nitrides and so called conchoidal fractures are formed. The tendency to forming the conchoidal fractures depends in particular on cooling rate (the casting modulus), aluminium and nitrogen contents in steel. During deoxidation, when manufacturing heavy castings, the elements with high affinity to nitrogen, zirconium or titanium, are added to steel that would decrease nitrogen activity by the bond on stable nitrides. The formation of stable nitrides should reduce the tendency of steel to the formation of conchoidal fractures. Deoxidation was thermodynamically analyzed at presence of the mentioned elements. For particular conditions a probable course of deoxidation was estimated at test castings. The deoxidation course was checked by microanalysis of deoxidation products (inclusions). For service and experimental castings the anticipated composition of inclusions was compared. It has been proved that in heavy castings with high aluminium contents in steel under studied conditions neither the addition of zirconium nor of titanium nor of rare earth metals will prevent the formation of conchoidal fractures.
Analysis of the use of the Russian materials (liquid glass and softening additives) has been made in accordance with the modern requirements for use in the technological processes of casting as binding materials in the production of large-sized steel railway casting. The reasons for poor knockout of liquid glass mixtures have been investigated. A complex action softening additive has been recommended for a better knocking-out ability. This solution provides a softening effect at the points of maximum formation of the liquid glass matrix strength in the processes of polymorphic transformation of the material under the influence of elevated temperatures as the result of filling the mold cavity by the melt. It has been shown that the use of additives of complex action leads to the decrease in the specific work of the knockout by four – seven times depending on the composition of the mixture and the design features of the casting. Experimental-industrial tests of the proposed method for softening the liquid glass mixtures have been made and the "Front Buffer Stop" casting has been made (for the rolling stock of locomotives and railway wagons). The tests confirmed the effectiveness and expediency of implementation of new liquid glass mixtures with softening additives in conditions of foundry enterprises.
This article proposes to use abrasive waterjet cutting (AWJ) for deflashing, deburring and similar finishing operations in casting. The basic requirements concerning the dimensional accuracy and surface texture of cast components are not met if visible surface flaws are detected. The experiments focused on the removal of external flash from elements made of EN-GJL-150 cast iron. The method employed for finishing was abrasive waterjet cutting. The tests were carried out using an APW 2010BB waterjet cutting machine. The form profiles before and after flash removal were determined with a Taylor Hobson PGI 1200 contact profiler. A Nikon AZ100 optical microscope was applied to observe and measure the changes in the flash height and width. The casting surface after finishing was smooth, without characteristic sharp, rough edges that occur in the cutting of objects with a considerable thickness. It should be emphasized that this method does not replace precise cutting operations. Yet, it can be successfully used to finish castings for which lower surface quality is required. An undoubted advantage of waterjet cutting is no effect of high temperature as is the case with plasma, laser or conventional cutting. This process is also easy to automate; one tool is needed to perform different finishing operations in order to obtain the desired dimensions, both internal and external.
In this paper the effects of titanium addition in an amount up to 0.13 wt.% have been investigated to determine their effect on the microstructure and mechanical properties of Thin Wall Vermicular Graphite Iron Castings (TWVGI). The study was performed for thinwalled iron castings with 3-5 mm wall thickness and for the reference casting with 13 mm. Microstructural changes were evaluated by analyzing quantitative data sets obtained by image analyzer and also using scanning electron microscope (SEM). Metallographic examinations show that in thin-walled castings there is a significant impact of titanium addition to vermicular graphite formation. Thinwalled castings with vermicular graphite have a homogeneous structure, free of chills, and good mechanical properties. It may predispose them as a potential use as substitutes for aluminum alloy castings in diverse applications.
While analyzing shape accuracy of ferroalloy precision castings in terms of ceramic moulds physical anisotropy, low-alloy steel castings ("cover") and cast iron ("plate") were included. The basic parameters in addition to the product linear shape accuracy are flatness deviations, especially due to the expanded flat surface which is cast plate. For mentioned castings surface micro-geometry analysis was also carried, favoring surface load capacity tp50 for Rmax = 50%. Surface load capacity tp50 obtained for the cast cover was compared with machined product, and casting plate surface was compared with wear part of the conveyor belt. The results were referred to anisotropy of ceramic moulds physical properties, which was evaluated by studying ceramic moulds samples in computer tomography equipment Metrotom 800.
Inconel 713C alloy belongs to the group of materials with high application potential in the aerospace industry. This nickel alloy has excellent features such as high strength, good surface stability, high creep and corrosion resistance. The paper presents the results of metallographic examinations of a base material and padding welds made by laser beam on the Inconel 713C alloy. The tests were made on precisely cast test plates imitating low - pressure turbine blades dedicated for the aerospace industry. Observations of the macro- and microstructure of the padding welds, heat-affected zone and base material indicate, that the Inconel 713C alloy should be classified as a hard-to-weld material. In the investigated joint, cracking of the material is disclosed mainly in the heat-affected zone and at the melted zone interface, where pad weld crystals formed on partially melted grains. The results show that phases rich with chromium and molybdenum were formed by high temperature during welding process, which was confirmed by EDS analysis of chemical composition.
The article presents a novel method that allows measurement of thermal conductivity that is based on Stefan-Boltzmann law. The developed method can be used to determine thermal conductivity of ceramic investment casting molds. The methodology for conducting thermal conductivity tests of ceramic material samples is presented. Knowledge of the value of thermal capacity and thermal conductivity as a function of temperature enables computer simulations of the process of cooling and solidification of liquid metal in a mold.
Air abrasion process is used for cleaning casting surface of prosthetic components, and to prepare the surface of these elements for the application of veneering items. Its side effect, however, is that abrasive particles are embedded in the treated surface, which can be up to 30% of the surface and it constitutes the side effect of this procedure. Such a significant participation of foreign material can not be indifferent to the properties of the surface. Embedded particles can be the place of stress concentration causing cracking of ceramics, and may deteriorate corrosion resistance by forming corrosive microlinks. In the latter cases, it would be advisable to remove elements embedded into the surface. The simplest method is chemical etching or electrochemical one. Nevertheless, these procedures should not significantly change the parameters of the surface. Among many possible reagents only a few fulfills all the above conditions. In addition, processing should not impair corrosion resistance of titanium, which is one of the most important factors determining its use as a prosthetic restoration in the mouth. The study presented results of corrosion resistance of titanium used to make prosthetic components by means of casting method, which were subjected to chemical processing designed to remove the embedded abrasive particles. The aim of the study was to investigate whether etching with selected reagents affects the corrosion resistance of titanium castings. For etching the following reagents were used: 30% HNO3 + 3% HF + H2O, HNO3+ HF+ glycerol (1:2:3), 4% HF in H2O2, 4% HF in H2O, with a control sandblasted sample, not subjected to etching. Tests demonstrated that the etching affected corrosion properties of test samples, in each case the reduction of the corrosion potential occurred - possibly due to the removal of particles of Al2O3 from the surface and activation of the surface. None of the samples underwent pitting corrosion as a result of polarization to 9 V. Values of the polarization resistance, and potentiodynamic characteristics indicated that the best corrosion resistance exhibited the samples after etching in a mixture of 4% solution of HF in H2O2. They showed very good passivation of the surface.
The article presents research results performed on aluminum bronze CuAl10Fe5Ni5 (BA1055) castings used for marine propellers. Metallographic studies were made on light microscope and a scanning electron microscope to assess quantitatively and qualitatively the alloy microstructure. It has been shown that the shape, size and distribution of the iron-rich κ−phase precipitates in bronze microstructure significantly affect its mechanical properties. With an increase in the number of small κ−phase precipitates increases the tensile strength of castings, while the presence of large globular precipitates improves ductility. Fragmentation and shape of κ−phase precipitates depends on many factors, particularly on the chemical composition of the alloy, Fe/Ni ratio, cooling rate and casting technology.
The article is a case study of the steel milling ring casting of about 6 tonnes net weight. The casting has been cast in the steel foundry the authors have been cooperating with. The aim was to analyse the influence of the shape of the chills and the material which was used to make them on the casting crystallization process. To optimally design the chills the set of the computer simulation has been carried out with 3 chills’ shape versions and 3 material’s versions and the results have been compared with the technology being in use (no chills). The proposed chills were of different thermal conductivity from low to high. Their shapes were obviously dependant on the adjacent casting surface geometry but were the result of the attempt to optimise their effect with the minimum weight, too. The chills working efficiency was analysed jointly with the previously designed top feeders system. The following parameters have been chosen to compare their effectiveness and the crystallization process: time to complete solidification and so-called fed volume describing the casting feeding efficiency. The computer simulations have been carried out with use of MagmaSoft v. 5.2 software. Finally, the optimisation has led to 15% better steel yield thanks to 60% top feeders weight reduction and 40% shorter solidification time. The steel ring cast with use of such technology fulfil all quality criteria.
In this work, the effects of 75 mm thick cast iron, (casting mould YIV) composition (Cu) and heat treatment were investigated on the microstructure and mechanical properties (hardness, elongation, tensile strength, yield strength) of ductile iron castings. As a result of adding Cu, the amount of pearlite is at 80% reduces of amount of ferrite. Normalizing of non-alloy cast iron increases the amount of pearlite to 70%. It also, increases tensile strength (659 MPa) and hardness (248 HB). Studied metallographic crossections were made from the grip sections of the tensile specimens. The structure composition and the characteristics of graphite were determined by computer image analysis. Measurements of graphite of non-alloy cast iron after normalizing and in cooper cast iron indicate the approximate amount of precipitates of graphite and their approximate average diameters. The applied normalizing and the additive alloy (Cu) were established to give comparable mechanical properties and structure of matrix in thick-walled castings.
Use of welding technology for the repair of steel castings is particularly common in two areas. These include weld surfacing of protrusions that remained incomplete after casting, or filling the surface defects (cavities). These defects are more common for steel casting than for graphite cast iron, due to the lower fluidity of steel. This article describes a suitable technological process of repairing the defects on the casting using the welding technology. A specimen produced for this purpose was prepared by carving a groove into a cast steel plate 20 GL, which was then filled with a weld metal using MAG (135) technology. The following evaluation of the basic characteristics of the repaired site point to the suitability of the selected technological parameters of the repair procedure. Metallographic evaluation was carried out, further evaluation of mechanical properties by tensile test, bend test and Vickers hardness test. The proposed methodology for the evaluation repair of foundry defects in steel castings also meets the requirements for the approval of welding procedures in accordance with the relevant valid legislation.
Simulation software dedicated for design of casting processes is usually tested and calibrated by comparisons of shrinkage defects distribution predicted by the modelling with that observed in real castings produced in a given foundry. However, a large amount of expertise obtained from different foundries, including especially made experiments, is available from literature, in the form of recommendations for design of the rigging systems. This kind of information can be also used for assessment of the simulation predictions. In the present work two parameters used in the design of feeding systems are considered: feeding ranges in horizontal and vertical plates as well as efficiency (yield) of feeders of various shapes. The simulation tests were conducted using especially designed steel and aluminium castings with risers and a commercial FDM based software. It was found that the simulations cannot predict appearance of shrinkage porosity in horizontal and vertical plates of even cross-sections which would mean, that the feeding ranges are practically unlimited. The yield of all types of feeders obtained from the simulations appeared to be much higher than that reported in the literature. It can be concluded that the feeding flow modelling included in the tested software does not reflect phenomena responsible for the feeding processes in real castings properly. Further tests, with different types of software and more fundamental studies on the feeding process modelling would be desirable.