An analysis has been carried out of the influence of annealing time at the preheating temperature of 650 °C on the change in hardness and alloy structure of lamellar graphite cast iron in the working as well as in the laboratory conditions. This preheat temperature is common during reclaiming welding of castings with complex shapes. The changes in unalloyed cast iron EN-GJL 200 to EN-GJL 300 according to ISO 1690 standard and cast iron with low amount of elements such as Sn, Cu, Cr, and Mo and their combinations were assessed. It was found that the cast iron of higher strength grades has better hardness and structural stability. Cast iron alloyed with chromium or its combinations has the highest stability. In unalloyed cast iron, a partial degradation of pearlite occurs; in alloyed cast iron the structural changes are not conclusive.
The paper presents the initial results of investigation concerning the abrasion resistance of cast iron with nodular, vermicular, or flake graphite. The nodular and vermicular cast iron specimens were cut out of test coupons of the IIb type with the wall thickness equal to 25 mm, while the specimens made of grey cast iron containing flake graphite were cut out either of special casts with 20 mm thick walls or of the original brake disk. The abrasion tests were carried out by means of the T-01M tribological unit working in the pin-on-disk configuration. The counterface specimens (i.e. the disks) were made of the JT6500 brand name friction material. Each specimen was abraded over a distance of 4000 m. The mass losses, both of the specimens and of the counterface disks, were determined by weighting. It was found that the least wear among the examined materials was exhibited by the nodular cast iron. In turn, the smallest abrasion resistance was found in vermicular cast iron and in cast iron containing flake graphite coming from the brake disk. However, while the three types of specimens (those taken from the nodular cast iron and from grey cast iron coming either from the special casts or from the brake disk) have almost purely pearlitic matrix (P95/Fe05), the vermicular cast iron matrix was composed of pearlite and ferrite occurring in the amounts of about 50% each (P50/Fe50). Additionally, it was found that the highest temperature at the cast iron/counterface disk contact point was reached during the tests held for the nodular cast iron, while the lowest one occurred for the case of specially cast grey iron.
The paper presents the results of investigations concerning the influence of gray cast iron modification on free vibration frequency of the disc casting. Three different chemical composition melts of gray cast iron were prepared in induction furnace. During gravity casting 0.05% and 0.3% mass of the Inolate modifier was added on stream of metal for changing graphite flakes in castings. Sound signal vibration of cast iron sample was registered by means on microphone for free vibration frequency measurements. Decreasing of free vibration frequency of modified cast iron in comparison with non modified castings was observed. Higher contents of modifier causes more decreasing of free vibration frequency. Cast iron with smaller contents of carbon and silicon have higher free vibration frequency in comparison with eutectic composition cast iron. Hardness of examined cast iron is lower when the more modifier is added during modification process. Free frequency is smaller with smaller Brinell hardness of disc casting. It was concluded that control of free vibration frequency of disc castings by means of chemical composition and modification process can improved comfort and safety of working parts.
The objective of the study reported in this paper was to determine the effect of structure on thermal power of cast-iron heat exchangers which in this case were furnace chambers constituting the main component of household fireplace-based heating systems and known commonly as fireplace inserts. For the purpose of relevant tests, plate-shaped castings were prepared of gray iron with flake graphite in pearlitic matrix (the material used to date typically for fireplace inserts) as well as similar castings of gray cast iron with vermicular graphite in pearlitic, ferritic-pearlitic, and ferritic matrix. For all the cast iron variants of different structures (graphite precipitate shapes and matrix type), calorimetric measurements were carried out consisting in determining the heat power which is quantity representing the rate of heat transfer to the ambient environment. It has been found that the value of the observed heat power was affected by both the shape of graphite precipitates and the type of alloy matrix. Higher thermal power values characterize plate castings of gray iron with vermicular graphite compared to plates cast of the flake graphite gray iron. In case of plates made of gray cast iron with vermicular graphite, the highest values of thermal power were observed for castings made of iron with ferritic matrix.
Results of a research on influence of chromium, molybdenum and aluminium on structure and selected mechanical properties of Ni-Mn-Cu cast iron in the as-cast and heat-treated conditions are presented. All raw castings showed austenitic matrix with relatively low hardness, making the material machinable. Additions of chromium and molybdenum resulted in higher inclination to hard spots. However, a small addition of aluminium slightly limited this tendency. Heat treatment consisting in soaking the castings at 500 °C for 4 h resulted in partial transformation of austenite to acicular, carbon-supersaturated ferrite, similar to the bainitic ferrite. A degree of this transformation depended not only on the nickel equivalent value (its lower value resulted in higher transformation degree), but also on concentrations of Cr and Mo (transformation degree increased with increasing total concentration of both elements). The castings with the highest hard spots degree showed the highest hardness, while hardness increase, caused by heat treatment, was the largest in the castings with the highest austenite transformation degree. Addition of Cr and Mo resulted in lower thermodynamic stability of austenite, so it appeared a favourable solution. For this reason, the castings containing the highest total amount of Cr and Mo with an addition of 0.4% Al (to reduce hard spots tendency) showed the highest tensile strength.
The paper includes validation studies of the flow module of the NovaFlow&Solid simulation code. Experiments of ductile iron and gray iron casting in a spiral test of castability were carried out. Casting experiments were then carried out in industrial conditions in the Ferrex Foundry in Poznań and the results are the castability spiral length and local cast iron rate during mould cavity pouring. Simulation tests using NovaFlow&Solid Control Volume code were made. The technological castability test was used to determine thermal-physical data through simplified inversion problem. Influence of physical parameters in the database of simulation code on the spiral length obtained as the result of simulation was analyzed. It was found that critical fraction of capillary flow CLFdown has the biggest impact on cast iron castability in the simulation code. The simulations resulted in defining parameters of gray iron GJL 250 and ductile iron GJS-400-15. For the parameters set, the length of castability spiral in simulations was in accordance with casting experiments.
In this work, the effects of 75 mm thick cast iron, (casting mould YIV) composition (Cu) and heat treatment were investigated on the microstructure and mechanical properties (hardness, elongation, tensile strength, yield strength) of ductile iron castings. As a result of adding Cu, the amount of pearlite is at 80% reduces of amount of ferrite. Normalizing of non-alloy cast iron increases the amount of pearlite to 70%. It also, increases tensile strength (659 MPa) and hardness (248 HB). Studied metallographic crossections were made from the grip sections of the tensile specimens. The structure composition and the characteristics of graphite were determined by computer image analysis. Measurements of graphite of non-alloy cast iron after normalizing and in cooper cast iron indicate the approximate amount of precipitates of graphite and their approximate average diameters. The applied normalizing and the additive alloy (Cu) were established to give comparable mechanical properties and structure of matrix in thick-walled castings.
The paper presents the results of experimental-simulation tests of expansion-shrinkage phenomena occurring in cast iron castings. The tests were based on the standard test for inspecting the tendency of steel-carbon alloys to create compacted discontinuities of the pipe shrinkage type. The cast alloy was a high-silicone ductile iron of GJS - 600 - 10 grade. The validation regarding correctness of prognoses of the shrinkage defects was applied mostly to the simulation code (system) NovaFlow & Solid CV (NFS CV). The obtained results were referred to the results obtained using the Procast system (macro- and micromodel). The analysis of sensitivity of the modules responsible for predicting the shrinkage discontinuities on selected pre-processing parameters was performed, focusing mostly on critical fractions concerning the feeding flows (mass and capillary) and variation of initial temperature of the alloy in the mould and heat transfer coefficient (HTC) on the casting - chill interface.
A significant development of the foundry industry contributes to the creation of high reliability and operational strength castings so that they meet specific standards in accordance with customers’ needs. This technology, however, is inseparably connected with casting defects in finished products. Cast products are subject to various defects which are considered acceptable or not, which is conditioned by the alloy chemical composition and strength characteristics, that is, generally – qualities to be agreed between the foundry and the customer. It is the latter that led the authors to research on designing a tool enabling the most reliable possible assessment of the emerging casting defects, which after proper consultations can be repaired and the casting – sold. The paper presents an original tool named the Open Atlas of Defects (OAD), developed for the last few years to support the evaluation of cast iron defects using Non-Destructive Testing (NDT) casting defects analysis tools (DCC card – Demerit Control Chart, Pareto-Lorenz analysis and ABC analysis). The OAD tool structure was presented as an integral part of the original system module for acquisition and data mining (A&DM) in conjunction with the possibilities of using selected tools for defect analysis support on the example of cast iron casting.
The paper presents results of the possibility of adapting the Althoff-Radtke test for High Chromium Cast Iron. The Althoff-Radtke test is a clump attempt used for steel. The Althoff-Radtke test has four different lengths of clamp which qualifies it as a test to quantitatively take into account different kinds of shrinkage ΔL. The length of the slot of the cracked corner and the length of each staple (50 - 350 mm) are the parameters tendency to cast cracks. Castings of white cast iron have a high tendency to hot cracking due to the large range of solidification temperatures, unfavorable kinetics parameters of shrinkage, and especially a lack of expansion before shrinkage. Shrinkage of high chromium white cast iron is similar to the shrinkage of cast steel, and is approximately 2%. Therefore it is important to test susceptibility to hot cracks. Research was carried out under industrial conditions. Four melts were performed, one of the initial chemical composition and the other three modified by different amounts of Fe-Ti, respectively, 0.25%, 0.5% and 0.75% Fe-Ti. The propensity for hot cracking was based on the observation of the dark surface in the corner of the sample. The study shows that the Althoff-Radtke test can be adapted to determine the tendency for hot cracking of high chromium cast iron. It should however be noted that the test results cannot be compared with those for other alloys.
The paper refers to previous publications of the author, focused on criteria of casting feeding, including the thermal criterion proposed by Niyama. On the basis of this criterion, present in the post-processing of practically all the simulation codes, danger of casting compactness (in the sense of soundness) in form of a microporosity, caused by the shrinkage phenomena, is predicted. The vast majority of publications in this field concerns shrinkage and feeding phenomena in the cast steel castings – these are the alloys, in which parallel expansion phenomenon does not occur as in the cast irons (graphite crystallization). The paper, basing on the simulation-experimental studies, presents problems of usability of a classic, definition-based approach to the Niyama criterion for the cast iron castings, especially of greater massiveness, for prediction of presence of zones of dispersed porosity, with relation to predictions of the shrinkage type defects. The graphite expansion and its influence on shrinkage compensation during solidification of eutectic is also discussed.
The validation of each simulation code used in foundry domain requires individual approach due to its specificity. This validation can by elaborated on the basis of experimental results or in particular cases by comparison the simulation results from different codes. The article concerns the influence of grey cast iron density curve and different forms of solid fraction curve Fs=f(T) on the formation of shrinkage discontinuities. Solid fraction curves applying Newtonian Thermal Analysis (NTA) were estimated. The experimental and numerical simulation tests were performed on the castings, which were made with Derivative Thermal Analysis (DerTA) standard cups. The numerical tests were realized using NovaFlow&Solid (NF&S), ProCast and Vulcan codes. In this work, the coupled influence of both curves on the dynamics of the shrinkage-expansion phenomena and on shrinkage defects prognosis in grey cast iron castings has been revealed. The final evaluation of the simulation systems usefulness should be based on validation experiment, preceded by comparing the simulation results of available systems which are proposed in given technology.