The paper deals with hypereutectic high chromium cast irons. The subject of examination was the effect of various alloying elements (Ti, W, Mo, V) on the size of primary carbides and on the resultant material hardness. Using a scanning electron microscope with a wave dispersion analyser, the carbon content in carbides was established. To determine the other elements, an energy dispersion analyser was used. It was found that both the primary and the eutectic carbides were of the M7C3 type and very similar in composition. The carbides always contained Cr and Fe, and also W, Mo, V or Ti, in dependence on the alloying elements used. The structure of materials containing only chromium without any alloying additions exhibited coarse acicular primary carbides. The structure of materials alloyed with another element was always finer. Marked refinement was obtained by Ti alloying.
Oxygen is an element that is first purposely brought into the steel melt to remove some unwanted elements or to reduce their concentration (oxidation). In the made cast steel there is on the contrary necessary to reduce the oxygen content with the use of deoxidation to such a level in order to avoid a reaction with carbon with the formation of CO bubbles. Concentration of oxygen in steel before casting is given, in particular, by the manner of metallurgical processing and the used deoxidation process. Oxygen is found in molten steels both as chemically bound in the form of oxides and in the form of oxygen dissolved in the solution – the melt. Chemical composition of the melt strongly influences the activity of oxygen dissolved in the melt and further on the composition of oxidic inclusions forming in the melt during the reaction with oxygen. In the Fe-C-Cr-Ni based alloys in the reaction with oxygen greatly participates also chrome, whose products are often in solid state and they are the cause of forming such defects as e.g. oxidic films.
Determination of the ferrite content in austenitic steels, which solidified under defined conditions. Ferrite content in austenitic matrix was determined from samples with wall thickness of 60 mm. Measured ferrite contents served to propose the regression equations for the calculation of the ferrite content in steels with Cr content of 18 up to 22 % and Ni of 9 up to 11 %. An additional regression equation was proposed for steels with a higher Ni content. The proposed regression equations have been checked up on the operating melts. In conclusion, the ferrite content in the axis of the casting of wall thickness of 500 mm has been calculated and it was compared to the ferrite determined in the usual way from the cast-on test.
The research was concerned with the influence of chemical composition of austenitic steels on their mechanical properties. Resulting properties of castings from austenitic steels are significantly influenced by the solidification time that affects the size of the primary grain as well as the layout of elements within the dendrite and its parts with regard to the last solidification points in the interdendritic melt. During solidification an intensive segregation of all admixtures occurs in the melt, which causes a whole range of serious metallurgical defects and it has also a significant influence on subsequent precipitation of carbides and intermetallic phases. Chemical heterogeneity then affects the structure and mechanical properties of the casting. In a planned experiment, we cast melted steels containing 18 to 28 % Cr and 8 to 28 % Ni with variable carbon and nitrogen contents. Testing the tensile strength of the cast specimens we could determine the Rp0.2, Rm, and A5 values. The dependence of the mechanical properties on the chemical content was described by regression equations. The planned experiment results allow us to control the chemical content for the given austenitic steel quality to achieve the required values of the mechanical properties.
The article deals with the influence of chemical composition of martensitic stainless steel for castings GXCrNi13-4 (the 1.4317 material) on mechanical properties and structure of as cast steel after heat treatment. Properties of these martensitic stainless steel are heavily influenced by chemical composition and structure of the material after heat treatment. Structure of these steels after quenching is formed with martensite and residual austenite. When tempering the steel the carbon content in martensite is reduced and gently deposited carbides occur. The way of heat treatment has a major impact on structure of martensitic steels with low carbon content and thus on strength, hardness and elongation to fracture of these steels. Chemical composition of the melt has been treated to the desired composition of the lower, middle and upper bounds of the nickel content in the steel within the limits allowed by the standard. Test blocks were gradually cast from the melt. The influence of the nickel equivalent value on structure and properties of the 1.4317 steel was determined from results of mechanical tests.
Heavy steel castings deoxidized with aluminium are sometimes brittle intercrystalline failed during their service along primary grain boundaries what is initiated by aluminium nitrides and so called conchoidal fractures are formed. The tendency to forming the conchoidal fractures depends in particular on cooling rate (the casting modulus), aluminium and nitrogen contents in steel. During deoxidation, when manufacturing heavy castings, the elements with high affinity to nitrogen, zirconium or titanium, are added to steel that would decrease nitrogen activity by the bond on stable nitrides. The formation of stable nitrides should reduce the tendency of steel to the formation of conchoidal fractures. Deoxidation was thermodynamically analyzed at presence of the mentioned elements. For particular conditions a probable course of deoxidation was estimated at test castings. The deoxidation course was checked by microanalysis of deoxidation products (inclusions). For service and experimental castings the anticipated composition of inclusions was compared. It has been proved that in heavy castings with high aluminium contents in steel under studied conditions neither the addition of zirconium nor of titanium nor of rare earth metals will prevent the formation of conchoidal fractures.
Compacted graphite iron, also known as vermicular cast iron or semiductile cast iron is a modern material, the production of which is increasing globaly. Recently this material has been very often used in automotive industry. This paper reviews some findigs gained during the development of the manufacturing technology of compacted graphite iron under the conditions in Slévárna Heunisch Brno, Ltd. The new technology assumes usage of cupola furnace for melting and is beeing developed for production of castings weighing up to 300 kilograms poured into bentonite sand moulds.