Twinned dendrites in Al-Zn alloy with high Zn content (40% wt.%) were successfully prepared by directional solidification. At different directional solidification rates (1000 and 1500 μm/s), microstructures and growth orientation variations of Al twinned dendrite and non-twinned dendrite were characterized. By using the inverted trapezoidal graphite sleeve at 1000 μm/s, Al twinned dendrite were formed to developed feather crystal structures in longitudinal section. Its primary and secondary twinned dendrite were grew along  direction. Moreover the deviation angle between  direction of Al twinned dendrite and the heat flow direction was about 27.15°. While not using the inverted trapezoidal graphite sleeve at 1000 and 1500 μm/s, Al dendrite was the non-twinned dendrite and the twinned dendrite was not appeared. The experimental results showed that the higher temperature gradient, a certain pulling rate and convection environment were the formation conditions of twinned dendrites.